Toward deformability enhancement of rare earth magnesium alloy by pulsed current

Di Wang,Shuyang Qin,Jingna Sun,Huagui Huang

DOI: https://doi.org/10.1016/j.msea.2023.145238

2023-06-05

Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing

Abstract:Here it was found that the pulsed current can improve the plasticity of Mg-13Gd-4Y–2Zn-0.5Zr rare earth magnesium alloy. When the parameters of pulsed current-assisted tension are 200 V; 100 μs; 2 Hz; 0.1 mm/min, the elongation can be increased from 3.6% to 10.4% but without strength loss. By comparing the mechanical properties of the samples under different frequencies, pulse widths and current densities, it was found that the current density is the most important factor, which can further improve the plasticity. Additionally, the basal texture strength decreased from 8.9 to 6.7, indicating that the anisotropy was weakened. The numerical calculation result showed that kinked lamellar long-period stacking ordered phases (LPSO) phases can lead to current distribution disorder inside grains, and it is difficult to form directional current at microscopic scale, so as to produce obvious texture. Besides, the grain size was refined from 50 μm to 12 μm after pulsed current-assisted tension, which is caused by the promoted dynamic recrystallization. This paper found a novel phenomenon based on the interaction between pulsed current and kinked lamellar LPSO phases inside grains, which can provide inspiration for deformation of rare earth magnesium alloys with low energy consumption and high efficiency, and it is an interesting subject.