Abstract:This study investigates the properties and performance of bismuth ferrite thin films on Kapton sheets as electromagnetic (EM) wave-absorbing materials. The main techniques employed in this study involved modifying the surface geometry and using electromagnetic wave-absorbing materials as surface coatings. X-ray diffraction analysis revealed a cubic crystal structure of the bismuth ferrite thin films. The bonding analysis showed the presence of Bi–O and Fe–O functional groups at 432.26 and 519.48 cm −1 , respectively. Vibrating-sample magnetometry revealed the ferromagnetic behavior of the bismuth ferrite thin film, confirming that saturation magnetization decreased with increasing sputtering time. Moreover, the calcination temperature affected the coercive field; the higher the calcination temperature, the higher the coercivity of the BiFeO 3 (BFO) thin film layer. Scanning electron microscopy with energy-dispersive X-ray spectroscopy of the bismuth ferrite thin films revealed the presence of Bi, Fe, and O—evenly and homogeneously distributed on the Kapton surface. After the ion implantation process, the atomic force microscopy test results showed an increased root-mean-square roughness ( Rq ). The root-mean-square roughness value for Kapton before the process was approximately 7.5 nm, while the root-mean-square roughness values for BFO 10 min and BFO 12.5 min were approximately 18.8 nm and 25.3 nm, respectively. The microwave absorption ability reached a maximum reflection loss value of − 40.4 dB (99.99 %) in the range of 9.98 GHz with a sputtering duration of 10 min. Therefore, these results suggest bismuth ferrite is a potential candidate as an EM wave absorber.

Electrical and optical properties of thin-film bismuth ferrite

Room Temperature Ferroelectric, Ferromagnetic and Magnetoelectric Properties of Ba-Doped Bifeo3 Thin Films

Study on dielectric, optic and magnetic properties of manganese and nickel co-doped bismuth ferrite thin film

Microstructures, magnetic, and microwave absorbing properties of ion-implanted bismuth ferrite thin films

Brief Theoretical Overview of Bi-Fe-O Based Thin Films

Ferroelectric and Photovoltaic Properties of Mn-Doped Bismuth Ferrite Thin Films

Exploring the Piezoelectric Properties of Bismuth Ferrite Thin Films Using Piezoelectric Force Microscopy: A Case Study

Magnetic And Electric Properties Of Fe3o4 Thin Films Sputtered On Metallic Underlayer

Research and Application of Barium Ferrite Thin Films

Spatially-Resolved Study of the Electronic Transport and Resistive Switching in Polycrystalline Bismuth Ferrite

Structural, dielectric, and electrical study of bismuth ferrite-lithium vanadate

Influence of barium doping on structural and magnetic properties of bismuth ferrite thin films via spray pyrolysis method

Study of optical and magnetic properties of Mn-substituted bismuth ferrite thin films

Faraday rotation spectra of bismuth-substituted ferrite garnet films with in-plane magnetization

Experimental and DFT investigation of structural and optical properties of lanthanum substituted bismuth ferrites

Internal friction in thin-film ferrite bismuth with an amorphous structure

Effects of Annealing Atmosphere on Microstructure, Electrical Properties and Domain Structure of Bifeo3 Thin Films

Investigation of electronic, ferroelectric and local electrical conduction behavior of RF sputtered BiFeO3 thin films

Effect of Pr and Mn Co-Substitution on Structural and Optical Properties of Bismuth Ferrite

Study of dielectric and impedance properties of Mn ferrites

Dielectric And Impedance Spectroscopic Studies Of Multiferroic BiFe1-xNixO3