Insight into the effect of In addition on hydrogen generation behavior and hydrolysis mechanism of Al‐based ternary alloys in distilled water—A new active Al‐Ga‐In hydrolysis hydrogen generation alloy
Yi Liu,Jun‐chao An,Wen‐zhong Jin,Jing Cui,Wei Zhang
DOI: https://doi.org/10.1002/er.4857
IF: 4.6
2019-09-12
International Journal of Energy Research
Abstract:<p>(Al2Ga)‐<i>x</i>In (<i>x</i> = 0, 2, 4, 6, 8 wt%) ternary aluminum (Al) alloys with different weight ratio of In for hydrolysis H<sub>2</sub> generation were prepared by melting‐casting technique. The phase compositions and microstructures of Al‐rich alloys were investigated by X‐ray diffraction (XRD) and high resolution scanning electron microscope (HR‐SEM) equipped with an energy dispersive spectrometer (EDS). The effect of In addition ratio on microstructures and H<sub>2</sub> generation performance were investigated, and the hydrolysis mechanism for Al‐Ga‐In ternary Al‐based alloys has been proposed. Al phase as matrix phase in the Al‐Ga‐In ternary alloy mainly determines the hydrolysis behavior, and the second phase In strongly promotes the hydrolysis process. The increase of In content can accelerate the H<sub>2</sub> generation rate as well as the final capacity and generation yield in neutral water. The generation yields for (Al2Ga)‐<i>x</i> In (<i>x</i> = 2, 4, 6, 8 wt%) alloys at 50°C are 0.56, 0.59, 0.62, and 0.66, respectively. The raising hydrolysis temperature can elevate the initial hydrolysis rate, final H<sub>2</sub> generation capacity, and yield. The H<sub>2</sub> generation capacities of (Al2Ga)‐8In alloy at 50°C, 60°C, and 70°C are 262, 290, and 779 mL·g<sup>−1</sup>, respectively.</p>
energy & fuels,nuclear science & technology