Abstract:International Journal of Modern Physics B, Ahead of Print. This study began by preparing gallium oxide (Ga2O3) doped with zinc fluoride (ZnF2) and manufacturing a target material. Subsequently, electron beam (e-beam) deposition was employed to coat silicon substrates with the prepared material. Different heat treatment conditions were applied to the deposited films, followed by material and electrical property analyses. The investigation explored the impact of pre-sintering Ga2O3 at 950°C to transform it into a more stable [math]-phase. For comparative purposes, some samples underwent annealing at 600°C in a nitrogen–hydrogen (95% N[math] H2, abbreviated as N[math]) mixed gas, which was used as a reduction atmosphere, to increase oxygen vacancies in the ZnF2-doped Ga2O3 thin films and consequently enhance their conductivity. The deposited ZnF2-doped Ga2O3 thin films initially exhibited an amorphous phase, with diffraction peaks appearing only after a 600°C annealing process. Pre-sintering Ga2O3 powder at 950°C promoted the emergence of the [math]-phase, and the bandgap value increased after annealing. Measurements using B1500A revealed that sintering and annealing ZnF2-doped Ga2O3 thin films were essential steps to enhance their conductivity. X-ray photoelectron spectroscopy (XPS) further confirmed a significant correlation between the conductivity variation and the concentration of oxygen vacancies. Additionally, it was observed that the use of an N[math] mixed gas further increased the presence of oxygen vacancies in the films. The results of this study provide an important method to make Ga2O3 thin films with conductivity, which can be utilized in the fabrication of Ga2O3 thin-film-based semiconductor devices in the future.

Examination of proper impurity doping and annealing conditions for solution processed Ga2O3 thin films

Atomic-Level Sn Doping Effect in Ga2O3 Films Using Plasma-Enhanced Atomic Layer Deposition

Controlled Crystallinity of a Sn-Doped α-Ga2O3 Epilayer Using Rapidly Annealed Double Buffer Layers

Influence of Nitrogen Annealing Treatment on Optical, Microstructural, and Chemical Properties of Ga2O3 Film Grown by Plasma-Enhanced Atomic Layer Deposition

Investigations of the growth and physical characteristics of ZNF2-DOPED GA2O3 thin films

Optical and Electrical Transport Properties of Α-Ga2o3 Thin Films with Electrical Compensation of Sn Impurities

The effect of annealing on the Sn-doped (−201) β-Ga2O3 bulk

Investigation of Solution-Processed Ga2O3 Thin Films and Their Application in Dielectric Materials

Annealing temperature controlled crystallization mechanism and properties of gallium oxide film in forming gas atmosphere

Precise control of the microstructural, optical, and electrical properties of ultrathin Ga2O3 film through nanomixing with few atom-thick SiO2 interlayer via plasma enhanced atomic layer deposition

Temperature-dependent oxygen annealing effect on the properties of Ga2O3 thin film deposited by atomic layer deposition

Effect of Process Conditions on the Transparent Conductive Properties Ga-Doped Thin Films

Synthesis of β-Ga2O3:Mg Thin Films by Electron Beam Evaporation and Postannealing

Improvement of crystal quality and UV transparence of dielectric Ga2O3 thin films via thermal annealing in N2 atmosphere

High Quality Heavy Sn Doping Β‑ga2o3 Film with High Mobility Grown by Time Division Transport Metal Organic Chemical Vapor Deposition

Effects of Sn Doping on the Electrical Performance and Stability of Sub-V Operating Metal-Oxide Thin-Film Transistors Fabricated by Oxygen Annealing

Chemical, Optical, and Electrical Characterization of Ga2O3 Thin Films Grown by Plasma-Enhanced Atomic Layer Deposition

Liquid Ga–In–Sn Alloy Printing of GaInSnO Ultrathin Semiconductor Films and Controllable Performance Field Effect Transistors

Thickness dependent optical properties of amorphous/polycrystalline Ga2O3 thin films grown by plasma-enhanced atomic layer deposition

The electrical conductivity of cubic (In$_{1-x}$Ga$_x$)$_2$O$_3$ films ($x\le0.18$): Native point defects, Sn-doping, and the surface electron accumulation layer

Comparative Study of High-Temperature Annealed and RTA Process β-Ga2O3 Thin Film by Sol–Gel Process