Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

Effects of axle load transfer on wheel rolling contact fatigue of high-power AC locomotives with oblique traction rods

Experimental study on wheel-rail rolling contact fatigue damage starting from surface defects under various operational conditions

Evolution of microscopic characteristics of rolling contact fatigue coexisting with wear of U75V rail

Impact of wheel profile evolution on wheel-rail dynamic interaction and surface initiated rolling contact fatigue in turnouts

Wear and RCF problems of metro wheel/rail systems: Phenomena, causes and countermeasures in China

Research on the damage mechanism of the rolling contact fatigue of a wheel–rail contact system under the influences of surface defects

On the Formation and Damage Mechanism of Rolling Contact Fatigue Surface Cracks of Wheel/rail under the Dry Condition

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Research on Rolling Contact Fatigue Failure of the Bearing Used in High-Speed Electric Multiple Units’ Axle Box Based on a Damage-Coupled Elastic–Plastic Constitutive Model

The Influence of Wheel Flats Formed from Different Braking Conditions on Rolling Contact Fatigue of Railway Wheel

Rail rolling contact fatigue formation and evolution with surface defects

Experimental characterization and numerical modeling on the external impacting of high-speed railway axle EA4T steel

Effect of normal load on the wear and rolling contact fatigue behaviour of AAR class B wheel against R350HT rail in a twin disc simulator

Corrosion fatigue behaviors and life prediction of railway axle EA4T steel with artificial indentation

Analysis on asymmetrical RCF cracks characterisation using an ACFM sensor and the influence of the rail head profile

Experimental and numerical insights into fatigue crack propagation of railway component with gradient residual stress

Effect of ultrasonic rolled material layer on the corrosion fatigue resistance of railway axle EA4T alloy steel

Enhancement of Fatigue Endurance Limit through Ultrasonic Surface Rolling Processing in EA4T Axle Steel

Fatigue life enhancement of foreign object impacted railway axle EA4T steel with surface shot peening

Wheel wear and rolling contact fatigue evolution under interaction of abrasive block and wheel–rail contact: results from field test

An investigation into Belgrospi-like damage formation on a sharp curved track using finite element method