Abstract:<p>We present a new theoretical and numerical framework for modelling mechanically-assisted corrosion in elastic–plastic solids. Both pitting and stress corrosion cracking (SCC) can be captured, as well as the pit-to-crack transition. Localised corrosion is assumed to be dissolution-driven and a formulation grounded upon the film rupture-dissolution-repassivation mechanism is presented to incorporate the influence of film passivation. The model incorporates, for the first time, the role of mechanical straining as the electrochemical driving force, accelerating corrosion kinetics. The computational complexities associated with tracking the evolving metal-electrolyte interface are resolved by making use of a phase field paradigm, enabling an accurate approximation of complex SCC morphologies. The coupled electro-chemo-mechanical formulation is numerically implemented using the finite element method and an implicit time integration scheme; displacements, phase field order parameter and concentration are the primary variables. Five case studies of particular interest are addressed to showcase the predictive capabilities of the model, revealing an excellent agreement with analytical solutions and experimental measurements. By modelling these paradigmatic 2D and 3D boundary value problems we show that our formulation can capture: (i) the transition from activation-controlled corrosion to diffusion-controlled corrosion, (ii) the sensitivity of interface kinetics to mechanical stresses and strains, (iii) the role of film passivation in reducing corrosion rates, and (iv) the dependence of the stability of the passive film to local strain rates. The influence of these factors in driving the shape change of SCC defects, including the pit-to-crack transition, is a natural outcome of the model, laying the foundations for a mechanistic assessment of engineering materials and structures.</p>

Chemo-mechanical coupling bond-based peridynamic model for electrochemical corrosion and stress chemical corrosion

A coupled mechano-chemical peridynamic model for pit-to-crack transition in stress-corrosion cracking

Study of mechano-electrochemical model: a numerical and experimental approach

A Corrosion Cracking Mechanism-Based Model with Molten Salt Corrosion Damage Coupling the Effect of Chloride Impurity and Plastic Deformation

A phase field formulation for dissolution-driven stress corrosion cracking

A microstructure-sensitive electro-chemo-mechanical phase-field model of pitting and stress corrosion cracking

Electro-chemo-mechanical phase field modeling of localized corrosion: theory and COMSOL implementation

Fully coupled peridynamic model for analyzing the chemo-diffusion-mechanical behavior of sulfate attack in concrete

Peridynamic Electromechanical Modeling of Damaging and Cracking in Conductive Composites: A Stochastically Homogenized Approach

A fully coupled meso-scale electro-chemo-mechanical phase field method for corrosion-induced fracture in concrete

Chemical Corrosion-Water-Confining Pressure Coupling Damage Constitutive Model of Rock Based on the SMP Strength Criterion

A phase-field chemo-mechanical model for corrosion-induced cracking in reinforced concrete

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

A mechanical-diffusive peridynamics coupling model for meso-scale simulation of chloride penetration in concrete under loadings

A chemo-mechanical coupling model for concrete lining subjected to external sulfate attack

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen

Modeling the Chemical-Mechanical Synergy During Copper CMP

A thermo-chemo-mechanically coupled peridynamics for investigating crack behavior in solids

Dynamic Electrochemical Model of Steel Corrosion in Concrete Microenvironment under Multifield Action of Heat-Moisture-Chlorine

Mechanical Properties and Statistical Damage Constitutive Model of Rock under a Coupled Chemical-Mechanical Condition

Development of a finite element model for simulation and prediction of mechanoelectrochemical effect of pipeline corrosion