Abstract:The paper considers the influence of the parameters of the plasma spraying process on the technological characteristics of multilayer coatings based on nickel-chromium, nickel-chromium-aluminum-yttrium materials, oxide ceramics, intended for operation at high temperature and additional dynamic loads. The design of plasma coatings during their application (with subsequent high-energy processing) under such conditions requires a comprehensive solution – both the use of high-quality powder ingredients and the optimization of technological parameters. The plasma process of applying powder materials has been improved to obtain the maximum values of their utilization factors. The technological characteristics that affect the properties of plasma coatings are optimized, namely: the flow rates of the plasma-forming and materials-transporting gases, the flow rate of supplied powder materials, the current and voltage of the electric arc of the plasma torch, the distance from the plasma torch nozzle exit to the substrate. The paper presents the results of studies of the structure of coatings, performed using scanning electron microscopy. Their analysis has made it possible to form general regularities obtained by the action of radiation of compression plasma flows on coatings formed by air plasma. The considered structures are created using the processes of melting, compaction and high-speed cooling of plasma coatings. The main optimization indicators are the maximum local compaction and spillage of the obtained compositions with the absence of defects and destruction from the impact of compression plasma flows. The main effect during the action of radiation of a compression plasma flow on previously formed coatings is thermal. It contributes heating of the near-surface layer. When the coating is exposed to radiation of compression plasma flows, a remelted layer of oxides with a thickness of about 12–15 μm is created, smoothing the relief of the formed surface and creating a network of cracks on the surface, diverging into the depth of the coating. The liquid-phase processes occurring in the molten phase of the near-surface layers after exposure to compression plasma radiation change the structure of the layers and contribute to the modification of their mechanical properties. By smoothing the surface, increasing the density of the surface crystallized layer and minimizing macro-defects – pores or macrocracks – the mechanical characteristics of the coatings increase.

Self-Propagating High Temperature Synthesis in Two-Layer (Ni + Al)/(PbO2 + B + Al2O3 + Glass) Powder Mixtures

Self-Propagating High-Temperature Synthesis of a Thin-Layer CuO–B–Glass System

Self-propagating high-temperature synthesis in a thin-layer CuO–B–glass system

Electrical insulation test of alumina coating fabricated by sol–gel method in molten PbLi pool

Self-Propagating High-Temperature Synthesis of Layered Composite Ti/Hf/Ta/Ni/Ceramics Materials

Thermal Explosion in a Powder Mixture of Aluminum with Nickel Preactivated in a Low-Energy Laboratory Mill

Consideration of Alumina Coating Fabricated by Sol-gel Method as MHD Coating against PbLi

Structure and Phase Formation in the Ni–Al–Co System during Self-Propagating High-Temperature Synthesis

Electron-Beam and Plasma Oxidation-Resistant and Thermal-Barrier Coatings Deposited on Turbine Blades Using Cast and Powder Ni(Co)CrAlY(Si) Alloys Produced by Electron Beam Melting IV. Chemical and Phase Composition and Structure of Cocralysi Powder Alloys and Their Use

Fabrication of a Novel MgO-B2O3-SiO2-Zn Coating by Thermal Spraying

Combustion synthesis of NiAl2O4 spinel powder

Step-wise exothermic reactions in pvd and cold-rolled Ni/Al multilayer foils

Preparation of an Aluminum Powder Composite with Double-Shell Nanostructure: Enhanced Thermal Conductivity Utilizing a Magnetic Orientation Effect

Welding in Ti–Al and Ni–Al Systems by Self-Propagating High-Temperature Synthesis

Architecture-independent reactivity tuning of Ni/Al multilayers by solid solution alloying

Multi-Layers Composite Plasma Coatings Based on Oxide Ceramics and M-Croll

Self-propagating high-temperature synthesis of MoAlB boride ceramics based on MAB-phase

Chemical composition, structure and microhardness of multilayer high-temperature coatings

MULTILAYER TUNGSTEN/QUASI-CRYSTAL Ti-Zr-Ni SYSTEMS AS PROMISING MATERIALS OF PROTECTIVE ELEMENTS A FUSION REACTOR

Al/AlN-based thermal paste fillers prepared by self-propagating high-temperature synthesis (SHS)

Effects of low-melting glass powder on the thermal stabilities of low infrared emissivity Al/polysiloxane coatings