Abstract:Molecular dynamics simulations are performed to investigate the thermochemical behavior of aluminum-coated nickel particles in the size range of 4–13 nm, beyond which asymptotic behavior is observed. The atomic interactions are captured using an embedded atom model. Emphasis is placed on the particle melting behavior, diffusion characteristics, and inter-metallic reactions. Results are compared with the corresponding properties of nickel-coated nano-aluminum particles. Melting of the shell, which is a heterogeneous process beginning at the outer surface of the particle, is followed by diffusion of aluminum and nickel atoms and inter-metallic reactions. The ensuing chemical energy heats up the particle under adiabatic conditions. The alloying reactions progressively transform the core–shell structured particle into a homogeneous alloy. The melting temperature of the shell is weakly dependent on the core size, but increases significantly with increasing shell thickness, from 750 K at 1 nm to 1,000 K at 3 nm. The core melts at a temperature comparable to the melting point of a nascent particle, contrary to the phenomenon of superheating observed for nickel-coated aluminum particles. The melting temperature of the core decreases from 1,730 to 1,500 K, when its diameter decreases from 10 to 7 nm. For smaller cores, the majority of nickel atoms participate in reactions before melting. The diffusion coefficient of nickel atoms in aluminum shell exhibits a temperature dependence of the form D = D0 exp(−EA/RT), with an activation energy of 43.65 kJ/mol and a pre-exponential factor of 1.77 × 10−7 m2/s. The adiabatic reaction temperature, also a size-dependent quantity, increases with increasing core diameter, attains a maximum value of 2,050 K at 5 nm, and decreases with further increase in the core diameter. The calculated values agree reasonably with those obtained via chemical equilibrium analysis. The burning time exhibits strong dependence of particle core size and shell thickness of the form τb = adcnδsm, where the exponents n and m are 1.70 and 1.38, respectively. The finding further corroborates the fact that the reaction rate is controlled by diffusion process.

Thermal Explosion in a Powder Mixture of Aluminum with Nickel Preactivated in a Low-Energy Laboratory Mill

Study on thermal explosion delay time of NiAl(Fe) system

Synthesis Of Nano-Nickel-Coated Micro-Aluminum And Thermal Reactivity Of Aluminum/Nickel-Stannic-Oxide Thermite

Synthesis of NiAl(Cr,Nb) Powder by Mechanical Alloying

Synthesis of bulk reactive Ni–Al composites using high pressure torsion

Dissolution–precipitation mechanism of self-propagating high-temperature synthesis of mononickel aluminide

The Effect of the Nickel Content and Mechanical Activation on Combustion in the 5Ti + 3Si + xNi System

Microstructure and formation mechanism of Ni-Al intermetallic compounds fabricated by reaction synthesis

Thermochemical behavior of nano-sized aluminum-coated nickel particles

Molecular Dynamics Simulation of Interdiffusion at the Initial Stage of High-Temperature Synthesis at the Dissolution of a Ni Nanoparticle in an Aluminum Matrix

The Effect of the Cobalt Content and Mechanical Activation on Combustion in the Ni + Al + Co System

In situ synchrotron X-ray diffraction study of synthesis reactions in mechanically activated Ti + Al powder mixture under linear heating conditions

Effect of Al Content on Reaction Laser Sintering of Ni-Al Powder

INFLUENCE OF MECHANICAL ACTIVATION ON REACTION ACTIVATION ENERGY OF Al-Ti-C POWDER MIXTURE IN SYNTHESIS PROCESS

Effect of self-propagating high-temperature combustion synthesis on the deposition of NiTi coating by cold spraying using mechanical alloying Ni/Ti powder

Synthesis of Nano-Size AlN Powders by Carbothermal Reduction from Plasma-Assisted Ball Milling Precursor

Step-wise exothermic reactions in pvd and cold-rolled Ni/Al multilayer foils

Formation of NiAl Intermetallic Compound by Cold Spraying of Ball-Milled Ni/Al Alloy Powder Through Postannealing Treatment

Study on combustion characteristics and pyrotechnic cutting effects of bimetal thermite Ni/Al/Fe2O3 system

Effect of deposited energy of wire electrical explosion in argon on characteristics of synthesized aluminum nanopowders

Kinetic parameters of the thermal explosion reaction of Ni-Al-Fe system