Abstract:In this study, structural, morphological, thermal and magnetic properties of amorphous-nanocrystalline Fe 70 Cr 10 Nb 10 B 10 (at.%) alloy are discussed. The formation and evaluation of amorphous-nanocrystalline structures of the alloy were followed by XRD, SEM-EDX, TEM, DTA, and VSM techniques. After 50 h of milling Cr, Nb, and B were completely dissolved into the Fe lattice forming 82% of the amorphous phase of the alloy. A gradual dissolution of the alloying elements also increased the lattice parameters concurrently. The lattice parameters reached a maximum value of 2.908 Å after 20 h of milling and then leveled off to a value of 2.891 Å at the end of 50 h of milling. Based on the XRD data, crystallite size and lattice strain of the alloy were calculated as 3.2 nm and 3.34% respectively. TEM analyses revealed that the alloy particulates comprised needle-shaped nanoparticles of an average size of 21 nm. The room temperature magnetic hysteresis loops showed that the increased duration of milling decreased the saturation magnetization from 91 to 24 emu/g. This was mainly due to the upsurge on the amorphous phase content in the alloy as the milling progressed. The increase in amorphous phase content and the subsequent reduction of the saturation magnetization were due to the inter-diffusion of the non-ferromagnetic Cr and B atoms into the Fe lattice. Thermal studies revealed that around 350 °C the amorphous phase of the alloy began crystallizing. The magnetic saturation of the heat-treated alloy also increased with the growth in the crystalline phases. The 50 h milled sample annealed at 700 °C was found to have the highest magnetic anisotropy as observed from the temperature-dependent zero-field cooled and field cooled magnetization measurements. The high-pressure X-ray diffraction measurements revealed that the amorphous state of the alloy remained stable up to 11.3 MPa. It also revealed the structural similarities of the Fe 70 Cr 10 Nb 10 B 10 alloy with those of the Fe 70 M 10 B 20 (M = Nb and Cr) types. For all practical purposes, the microstructural stability under high compressive pressure represents the consolidation properties of the nanostructured magnetic materials since both pressure and temperature-induced phase transformations are the primary controlling factors for the specific magnetization properties of the alloy.

Synthesis and magnetic properties of Ni3Fe intermetallic compound obtained by mechanical alloying

Nanocrystalline Ni-30wt%Fe Supersaturated Solid Solution Synthesized by Mechanical Alloying

Research of nanocrystalline Ni-30%Fe solid solution synthesized by mechanical milling

Magnetic properties and Structural characterization of nanocrystalline Fe-20%A (Ni, Co and Si) alloys powders synthesized by mechanical alloying process

Magnetic and Microstructural Properties of Nanostructured/Amorphous NiTi Prepared by Mechanical Alloying

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

Microstructural and Magnetic Characteristics of High-Entropy FeCoNiMnTi Alloy Produced via Mechanical Alloying

Influence of Milling Time on the Microstructure and Soft-Magnetic Properties of Nanocrystalline Fe72Ni8Co8Zr7B4Cu1

The Effect of B and Si Additions on the Structural and Magnetic Behavior of Fe-Co-Ni Alloy Prepared by High-energy Mechanical Milling

Research on Fe-10%Ni Alloy Synthesized by Mechanical Alloying

Direct Synthesis of MgCNi3 by Mechanical Alloying

Structural and thermal properties of the Fe-based alloys prepared by mechanical milling

The Morphology and Microstructure of Nanocrystalline Fe1-x-Nix Alloy Powders by Mechanical Alloying

Synthesis and characterization of amorphous-nanocrystalline Fe70Cr10Nb10B10 powders by mechanical alloying

Microstructure and Magnetic Properties of Nanocrystalline Fe60−xCo25Ni15Six Alloy Elaborated by High-Energy Mechanical Milling

Experimental and computational investigations on mechanically alloyed Fe55Co30Ni15 powders

Synthesis of NiAl(Cr,Nb) Powder by Mechanical Alloying

The Effect of Mechanical Alloying Technology on Microstrcture of Fe-Ni Alloy

Ni 3 Fe/Cr nanocrystalline soft magnetic composite compacts obtained by mechanical milling and spark plasma sintering

Microstructures of Mechanically Alloyed Fe60Ni40 Studied by XAFS and XRD

Mechanochemical synthesis of nanocrystalline Ni-Zn ferrite