Abstract:Printed electronics are circuits that are additively manufactured using conductive pastes composed of micro-/nanoconductive metal particles. Silver-based compounds are the most widely used metals for such pastes due to their superior conductivity and oxidation stability. However, the high cost of silver (Ag) has demanded its replacement with more cost-effective and abundant metals such as copper (Cu). Despite its cost-effectiveness and abundance, Cu suffers from high oxidation tendency and sintering temperature that have limited its widespread utilization in printed electronics. In this work, we have developed a low-cost hybrid bimodal paste composed of Cu microparticles (1–5 μm) and Ag nanoparticles (20–30 nm) (CuMPs/AgNPs) via nondestructive photonic sintering. The concurrent melting of AgNPs and catalytic reduction of CuMPs allow the paste to be sintered at considerably low temperatures using an intense-pulsed light (IPL) source. The required light energy density for effective sintering of different mixing ratios of AgNPs and CuMPs was systematically measured using electrical, optical, and mechanical characterization techniques. These analyses revealed that a minimum of 16 wt % AgNPs in the bimodal CuMP/AgNP paste with an IPL irradiation energy of 10.6 J/cm2 and pulse duration of 5 ms achieved a minimum sheet resistance of 0.072 Ω/□ that results from localized melting of AgNPs between adjacent CuMPs. Furthermore, the CuMP/AgNP films with a minimum of 6 wt % AgNPs showed significantly improved oxidation stability characteristics even after 7 days of incubation in accelerated oxidation conditions [70 °C and 100% relative humidity (RH)]. As a proof of concept, we demonstrated an application of the developed paste (CuMPs-6 wt % AgNPs) by directly printing a wireless resonant moisture sensor onto the interior region of a cardboard package box, which is capable of performing in situ monitoring of the moisture ranging from 30 to 85% RH with an average linear sensitivity of −3.08 % RH/MHz.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaelm.1c00345.Thermal behavior of PVP, effect of drying temperature and duration on sheet resistance of the oven-dried CuMPs-6 wt % AgNP printed trace, followed by photonic sintering with optimum setting of two pulses at 10.6 J/cm2 energy, effect of EG on sheet resistance of the paste with CuMPs-6 wt % AgNP and CuMPs-16 wt % AgNP compositions, reoxidation, and damage assessment of the hybrid bimodal paste after photonic sintering with excessive thermal energy, effect of increasing thermal energy on sheet resistance of CuMPs-0 wt % AgNP printed trace EDX spectrum and elemental composition analysis (at %) of the photonically sintered CuMPs-16 wt % AgNP printed trace with optimum settings, and 3D confocal microscopy analysis of CuMPs-20 wt % AgNP printed trace (PDF)This article has not yet been cited by other publications.

Copper nanoparticle conductive patterns fabricated by thermal sintering using carboxylic acid vapors and their application for radio-frequency identification antennas

Preparation of Conductive Cu Patterns by Directly Writing Using Nano-Cu Ink

Synthesis and Characterization of Air-Stable Cu Nanoparticles for Conductive Pattern Drawing Directly on Paper Substrates

Copper nanoparticles: aqueous phase synthesis and conductive films fabrication at low sintering temperature.

One-step Synthesis of Ag Nanoparticles for Fabricating Highly Conductive Patterns Using Infrared Sintering

Ambient Aqueous-Phase Synthesis of Copper Nanoparticles and Nanopastes with Low-Temperature Sintering and Ultra-High Bonding Abilities

Rapid Low Temperature Sintering in Air of Copper Submicron Particles with Synergistic Surface-Activation and Anti-Oxidative Protection

Nanoporous Copper Pattern Fabricated by Electron Beam Irradiation on Cu3N Film for SERS Application

Synthesis of Stable Ultra-Small Cu Nanoparticles for Direct Writing Flexible Electronics

Reactive Sintering of Cu Nanoparticles at Ambient Conditions for Printed Electronics

Room Temperature Sintering of Cu-Ag Core-Shell Nanoparticles Conductive Inks for Printed Electronics

Self-reducible copper inks composed of copper–amino complexes and preset submicron copper seeds for thick conductive patterns on a flexible substrate

Highly Conductive Copper–Silver Bimodal Paste for Low-Cost Printed Electronics

A Green Method for Synthesizing Novel Nanoparticles and Their Application in Flexible Conductive Patterns

Thermal Analysis of Cu-Organic Composite Nanoparticles and Fabrication of Highly Conductive Copper Films

Isotropically Conductive Adhesives Filled with Copper Nanoparticles and Micron-Sized Flakes

Flexible and Transparent Cu Electronics by Low‐Temperature Acid‐Assisted Laser Processing of Cu Nanoparticles

In-air sintering of copper nanoparticle paste with pressure-assistance for die attachment in high power electronics

A mild aqueous synthesis of ligand-free copper nanoparticles for low temperature sintering nanopastes with nickel salt assistance

Anti-oxidative Copper Nanoparticle Paste for Cu–Cu Bonding at Low Temperature in Air

Copper conductive adhesives for printed circuit interconnects