Abstract:Conductive copper nanoinks can be used as a low-cost replacement for silver and gold nanoinks that are used in inkjet printing of conductive patterns. We describe a high-throughput, simple, and convenient method for the preparation of copper nanoparticles in aqueous solution at room temperature. Copper acetate is used as the precursor, hydrazine as the reducing agent, and short chain carboxylic acids as capping agents. The concentration of the carboxylic acid plays a key role in the preparation of such copper nanoparticles. Stable copper nanoparticles with a diameter of less than 10 nm and a narrow size distribution were prepared when high concentrations of lactic acid, citric acid, or alanine were used. Thermogravimetric analysis results showed that any lactic acid or glycolic acid adsorbed on the surface of the copper nanoparticles can be removed at a relatively low temperature, especially, glycolic acid, which can be removed from the surface at about 125 °C. Highly conductive copper films prepared using lactic acid and glycolic acid as capping agents were obtained by drop coating a copper nanoparticle paste onto a glass slide followed by low temperature sintering. The electrical resistivity of the copper film using glycolic acid as the capping agent was 25.5 ± 8.0 and 34.8 ± 9.0 μΩ·cm after annealing at 150 and 200 °C for 60 min under nitrogen, respectively. When lactic acid was used as the capping agent, the electrical resistivity of the copper films was 21.0 ± 7.0 and 9.1 ± 2.0 μΩ·cm after annealing at 150 and 200 °C for 60 min under nitrogen, respectively, with the latter being about five times greater than the resistivity of bulk copper (1.7 μΩ·cm).

A Green Method for Synthesizing Novel Nanoparticles and Their Application in Flexible Conductive Patterns

One-step Synthesis of Ag Nanoparticles for Fabricating Highly Conductive Patterns Using Infrared Sintering

Facile Synthesis of Silver Nanoparticles and Preparation of Conductive Ink

Synthesis of stable CucoreAgshell&Ag particles for direct writing flexible paper-based electronics

Green Synthesis of Micron-Sized Silver Flakes and Their Application in Conductive Ink

Facile Preparation of Monodisperse Cu@Ag Core–Shell Nanoparticles for Conductive Ink in Printing Electronics

Reactive Sintering of Cu Nanoparticles at Ambient Conditions for Printed Electronics

Synthesis of Stable Ultra-Small Cu Nanoparticles for Direct Writing Flexible Electronics

Room Temperature Sintering of Cu-Ag Core-Shell Nanoparticles Conductive Inks for Printed Electronics

Synthesis and Characterization of Air-Stable Cu Nanoparticles for Conductive Pattern Drawing Directly on Paper Substrates

Preparation of Conductive Cu Patterns by Directly Writing Using Nano-Cu Ink

Facile synthesis of monodisperse silver nanoparticles for screen printing conductive inks

Copper nanoparticles: aqueous phase synthesis and conductive films fabrication at low sintering temperature.

Sintering mechanism of size-controllable Cu-Ag core–shell nanoparticles for flexible conductive film with high conductivity, antioxidation, and electrochemical migration resistance

Optical Printing of Conductive Silver on Ultrasmooth Nanocellulose Paper for Flexible Electronics

Green Approach to Prepare Silver Nanoink with Potentially High Conductivity for Printed Electronics

The Fabrication, Properties, and Application of a Printed Green Ag NWs-Based Flexible Electrode and Circuit

Facile synthesis of low temperature sintering Ag nanopaticles for printed flexible electronics

Ingenious Method for Rapid Fabrication of a Highly Conductive Hybrid Film of Printed Cu Nanoparticle Layers Plated by Ag Nanoplates on a PET Substrate at Room Temperature

Controlling the Structures, Flexibility, Conductivity Stability of Three-Dimensional Conductive Networks of Silver Nanoparticles/Carbon-Based Nanomaterials with Nanodispersion and their Application in Wearable Electronic Sensors

Nano-Silver Ink of High Conductivity and Low Sintering Temperature for Paper Electronics