Abstract:Because of the high specific surface area and enhanced charge migration, TiO2 with unique belt-like nanostructures finds promising applications in various fields such as photocatalysis, dye-sensitized solar cells, gas sensors, and Li-ion batteries. In the current study, a solution combustion procedure was firstly adopted to prepare a black water-proof precursor. The black precursor interacted with H2O2 at ambient temperature, achieving a precursor solution that is capable of fabricating hydrogen titanate (H2Ti2O5·H2O) nanobelt arrays on metallic Ti substrates at 60 °C. Subsequent calcination in air at 400 °C achieved arrays of ultrathin anatase TiO2 nanobelts of ca. 2–4 nm in thickness. The addition of nickel nitrate in the combustion solution achieved the Ni-doping into the resultant TiO2 nanobelts, which did not alter the nanobelt structure but significantly reduced the band gap from 3.2 eV to 2.9 eV. When compared with the commonly alkali-hydrothermal synthesized anatase TiO2 nanobelts, the present ultrathin nanobelts exhibited much improved photocatalytic activity when utilized to assist photodegradation of rhodamine B in water. The ultrathin nanobelt structure is believed to contribute to the high specific surface area, the much reduced charge migration path, and the enhanced charge transport along the longitudinal direction. The appropriate Ni-doping further enhanced the photocatalytic performance, because of the increased light harvesting efficiency and reduced charge recombination.

Preparation and photocatalytic properties of DBD plasma F/N co-doping modified TiO2

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Microstructures and Properties of N-Doped TiO_2 Films Grown by Dielectric Barrier Discharge Chemical Vapor Deposition

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Photonic, and Photocatalytic Behavior of Tio2 Mediated by Fe, Co, Ni, N Doping and Co-Doping

Microstructure and Properties of N-Doped TiO_2 Films Grown by Dielectric Barrier Discharge Enhanced Chemical Vapor Deposition（DBD-CVD）

Characterization and photocatalytic activity of Ni-doped tiO2 nano photocatalysts prepared by low temperature combustion synthesis]

Preparation and Properties of N -Doped TiO2 Films by APCVD

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Phenol Degradation by TiO2 Photocatalysts Combined with Different Pulsed Discharge Systems.

Photocatalytic Activity of Nitrogen Doped Nano-titanias and Titanium Nitride towards Methylene Blue Decolouration

Confined Preparation of N-doped Commercial P25 TiO2 Photocatalysts with Fast Charge Separation by Argon-diluted Nitrogen Plasma Treatment

Preparation and photocatalysis property of N-doped TiO2 film

TiO x N y Modified TiO 2 Powders Prepared by Plasma Enhanced Atomic Layer Deposition for Highly Visible Light Photocatalysis

Interstitial N-Doped TiO2 for Photocatalytic Methylene Blue Degradation under Visible Light Irradiation

Preparation of Lif-Doped Tio2 and Its Photocatalytic Performance for Degradation of Methylene Blue

Photocatalytic TiO₂ Nanoparticles Activated by Dielectric Barrier Discharge Plasma Assisted Ball Milling

Co-Modified Commercial P25 Tio2 by Fe Doping and G-C3n4 Coating As High Performance Photocatalyst under Visible Light Irradiation

Preparation,characterization and photocatalytic property of effective Fe~(3+),Zn~(2+) co-doped nano-TiO_2

Preparation and Photocatalytic Activity of Nanoparticle Fe/TiO2 by Chemical Precipitation Method

Dielectric barrier discharge plasma-assisted modification of g-C3N4/Ag2O/TiO2-NRs composite enhanced photoelectrocatalytic activity