Effect of Al atomic layer on the wetting behavior, interface structure and electrical contact properties of silver reinforced by Ti3AlC2 ceramic
Kuankuan Ding,Kaige Zhang,Jianxiang Ding,Xiao Zhang,Xinxin Xia,Liming Chen,Songlin Ran,Chengjian Ma,Li Yang,Peigen Zhang,ZhengMing Sun
DOI: https://doi.org/10.1016/j.ceramint.2021.08.378
IF: 5.532
2022-01-01
Ceramics International
Abstract:Ti3AlC2 ceramic exhibits potential in Ag-based composite electrical contact materials, but its interface characteristic with Ag matrix remains unexplored. In this work, sessile drop experiment is carried out to investigate the high-temperature wetting behavior of molten Ag with Ti3AlC2. Stable Ti3AlC2 is hardly wetted by molten Ag below 1000 °C(contact angle of 148.5°), but the wettability of Ag/Ti3AlC2 improves with the increasing temperature(final 14° at ∼1130 °C). In contrast, the Ti3C2, a MXene with Al layer removed from its parent Ti3AlC2, exhibits inferior wettability with Ag(final 56.5° at ∼1130 °C). Wetting mechanism of Ag/Ti3AlC2 is proposed on the basis of the interfacial structure and chemical composition. Increasing temperature accelerates dissociation of Ti3AlC2, and outward-escaping Al reacts with Ag to form interface layer with a composition of Ag4.86Ti8.66AlC7.59, Ag also diffuses along Ti3AlC2 grain boundaries and forms gradient reactive products(Ag–Ti–Al–C), which promotes their wettability. Finally comprehensive properties of Ag/Ti3AlC2 and Ag/Ti3C2 are compared. Al–Ag interdiffusion slightly decreases the electrical conductivity of Ag/Ti3AlC2 bulk material, but strengthen the interface bonding of composite and promote the viscosity of the molten pool, leading to the superior mechanical and anti-arc erosion properties. Absence of Al–Ag interdiffusion does remarkably improve the electrical conductivity of Ag/Ti3C2 bulk materials, but lack of Al layer damages the mechanical core and wettability with Ag, resulting in a drastic decrease of anti-arco erosion property.
materials science, ceramics