Abstract:In this document, RF magnetron sputtering to generate a set of composite coatings comprising MoN and Ag, exhibiting diverse concentrations of silver (Ag). Comprehensive investigations were conducted to scrutinize the coatings, encompassing an examination of their microstructure, mechanical attributes, and tribological performance. This multi-faceted analysis leveraged state-of-the-art techniques, such as XRD, SEM, HRTEM, EDS, etc. Our research findings suggest that the MoN-Ag coatings revealed a composite composition, comprising structures of fcc-Mo 2 N and fcc-Ag. As the Ag content was elevated, the coating’s hardness initially exhibited a gradual augmentation before subsequently declining after reaching its zenith, with the highest hardness recorded at 26.7 GPa. At room temperature, the MoN-Ag coating displayed a distinctive tribological behavior, where the average friction coefficient experienced an initial rapid reduction followed by a gradual increment. Notably, the coefficient reached its nadir at 0.38 with an Ag content of 3.90 at.%. Moreover, the wear rate of the coatings exhibited a similar trend, registering a slight decline followed by an increase as the Ag content was augmented, with the lowest recorded value being 1.63×10 −8 mm 3 N −1 mm −1 at an Ag content of 1.61 at.%. In the case of MoN-Ag coatings, the average friction coefficient initially exhibited an increase, followed by a swift decline as the temperature rose from ambient to higher levels. This coefficient reached its lowest value, 0.29, at 600 °C. In contrast, the wear rate showed a steady escalation in line with the temperature increase, peaking at a maximum of 2.77×10 −7 mm 3 N −1 mm −1 at 600 °C.

Influence of Ag Contents on Structure and Tribological Properties of TiSiN-Ag Nanocomposite Coatings on Ti–6Al–4V

Influence of multi-interfacial structure on mechanical and tribological properties of TiSiN/Ag multilayer coatings

Structure, Mechanical and Tribological Properties of Self-Toughening TiSiN/Ag Multilayer Coatings on Ti6Al4V Prepared by Arc Ion Plating

Microstructure and high-temperature tribological properties of TiSiN-Ag coatings deposited by multi-arc ion plating

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Microstructure, mechanical properties and tribological behaviors of TiAlN-Ag composite coatings by pulsed magnetron sputtering method

Influence Of Annealing Temperature On Film Morphology And Tribological Performance Of Tisin-Ag Coating

Influence of Si Content on Microstructure and Mechanical Properties of TiAlSiN Nanocomposite Coatings

The Influences of Ag Content on the Friction and Wear Properties of TiCN–Ag Films

Insight into the Influence of Ag Contents on Microstructure, Mechanical and Tribological Performance of MoN-Ag Coatings

Microstructure and Tribology of TiC(Ag)/a-C:H Nanocomposite Coatings Deposited by Unbalanced Magnetron Sputtering

Effect of Multi-Interfacial Structure on Fracture Resistance of Composite TiSiN/Ag/TiSiN Multilayer Coating

Effect of Ag Content on Friction and Wear Properties of TiCN/Ag Films in Different Service Environments

Preparation and Tribological Behavior of Ti2AlNb/Ag Self-Lubricating Composites

Effect of Ag Content on Friction and Wear Properties of Ag and V Co-Doped CrN Coatings at 25–700 °C

Effect of Ti Content on the Microstructure and Mechanical Properties of TiAlSiN Nanocomposite Coatings

Effect of Ag Doping on the Microstructure and Electrochemical Response of TiAlN Coatings Deposited by DCMS/HiPIMS Magnetron Sputtering

Effects of nanocrystalline silver incorporation on sliding tribological properties of Ag-containing diamond-like carbon films in multi-ion beam assisted deposition

Effect of silver content on the microstructure, thermal stability and mechanical properties of CrNx/Ag nanocomposite films

Effect of Ag Content on Microstructure and Tribological Performance of WS2–Ag Composite Films

Influence of Ag Content and Nanograin Size on Microstructure, Mechanical and Sliding Tribological Behaviors of Ag-DLC Films.