The Effect of ZnO Nanoparticles on Weathering Performance of Wood Plastic Composites

Sefa Durmaz,Ozlem Ozgenc Keles,Ugur Aras,Yusuf Ziya Erdil,Fatih Mengeloglu

DOI: https://doi.org/10.1111/cote.12666

2022-12-15

Coloration Technology

Abstract:In recent years, wood‐plastic composites (WPCs) have become among the most popular engineering materials. Most of their usage areas are outdoors, in which they encounter various damaging factors. The weathering conditions cause significant deterioration to WPC surfaces, which negatively influences their service life. In this study, ZnO nanoparticles at different concentrations (1, 3, 5, 10%) were added to the high density polyethylene (HDPE) based WPC matrix. The effect of ZnO nanoparticles on the weathering performance of WPC was evaluated after 840 h of the artificial weathering test. The highest color changes (∆E*) were monitored with control samples exposed for 840 h. Adding ZnO nanoparticles improved the UV resistance and decreased the color changes. The wood flour content also affected the color changes on the WPC surface. The 10% ZnO nanoparticles and 50% wood flour content provided the lowest color changes. The barrier effect of nanoparticles prevented the WPC surface from UV lights. ZnO nanoparticles also positively affected the load transfer, which restricted the reduction in the mechanical properties after the weathering test. The degradation on the surface of WPCs has also been investigated by ATR‐FTIR analysis. The changes in the characteristic bands of polymer and wood indicated that surface degradation was inevitable. The light (LM) and scanning electron microscopy (SEM) images also demonstrated micro‐cracks and roughness on the surface of WPCs. It is concluded that UV degradation is unavoidable, but ZnO nanoparticles could improve surface resistance against weathering conditions. This article is protected by copyright. All rights reserved.

engineering, chemical,chemistry, applied,materials science, textiles