Abstract:Hot-stamped ultrahigh strength steel components are pivotal to automotive light-weighting. Steel blanks, often coated with an aluminum-silicon (Al-Si) layer to protect them from oxidation and decarburization, are austenitized within a furnace and then simultaneously quenched and formed into shape. The Al-Si coating melts within the furnace and reacts with iron from the steel to yield an intermetallic phase that provides some long-term corrosion protection. During the intermediate liquid phase, some of the coating may transfer to the furnace components, leading to maintenance costs and operational downtime. A detailed understanding of the coating transformation mechanism is needed to avoid such production issues while ensuring that final intermetallic coatings conform to specifications. We introduce cross-sectional Raman microscopic mapping as a method to rapidly elucidate the coating transformation mechanism. Raman spectroscopic fingerprints for relevant intermetallic compounds were determined using synthesized Al-Fe-Si ternary and Al-Fe binary compounds. These fingerprints were used to map the spatial distribution of intermetallic compounds through cross sections of Al-Si-coated 22MnB5 specimens that were heated at temperatures between 570 and 900 °C. These chemical maps show that the intermetallic fraction of the coating does not grow significantly until formation of η (Al5Fe2) at the steel interface, suggesting that η facilitates extraction of iron from the steel and subsequent diffusion through the coating. Under the heating conditions used here, a series of reactions ultimately lead to a silicon-rich τ2 (Al3FeSi) phase on top of the binary η phase. The technique presented here simplifies structural analysis of intermetallic compounds, which will facilitate prototyping of strategies to optimize hot stamping.

Preparation Method for Metallographic Specimen of Iron-Carbon and Silicon-aluminium Alloy

The Study of Ferrosilicon Alloy Sediment Horizon Metallographic Etchant

Metallographic Practices Generally Applicable to All Metals

Metallographic Specimen Preparation: Optical And Electron Microscopy

Preparation of metallographic specimen of superficial ferrite by using low carbon steel

Microstructure Characterization of W-Ni-Fe Heavy Alloys with Optimized Metallographic Preparation Method

A Few Preparation Methods and Their Delication Mechanism for High-silicon Aluminum Alloy

ETCHING METHOD OF LAMINAR MATEL COMPOSITES METALLOGRAPHIC SPECIMEN

Microstructure and Mechanical Properties of Sic/Al Nanocomposite

The Choice of Metallographic Corrosive in the Sample of Electro-Deposition Silicon Steel Section

Specimen Preparation of Aluminum Alloy Powders for Transmission Electron Microscopy

Corrosion Behaviour of AZ91DSm<sub>1.0</sub> with Different Preparation Methods

Study on Microstructure and Mechanical Properties of Al-Si-Cu-Mg Alloy Prepared by Casting and Powder Metallurgy

The Analysis of the Surface Defects of the AlMg10 Alloy Parts

Metallurgical Process Analysis and Microstructure Characterization of the Bonding Interface of QAl9-4 Aluminum Bronze and 304 Stainless Steel Composite Materials

Raman Spectroscopic Analysis of the Reaction between Al-Si Coatings and Steel

Research Progress on Microstructure and Corrosion Behavior of Selective Laser Melted Al-Si Alloys

Preparation of Mg-15%Al-5%Si-0.5%Sb alloy and its microstructure

Characteristics of Metal Specimens Formed by Selective Laser Melting: A State-of-the-Art Review

PREPARATION TECHNOLOGIES FOR PARTICLE REINFORCED ZA ALLOYS COMPOSITES

Microstructure and Fracture Behavior of Al‐Si‐Mg Alloy Prepared with Recycled Alloy