Improving the electrochemical performance of Ni-rich LiNi0.6Co0.2Mn0.2O2 cathode at high cutoff voltage coated with LiBO2

Wentao Zhao,Hailang Zhang,Huapeng Yang

DOI: https://doi.org/10.1007/s11581-022-04724-y

IF: 2.961

2022-10-13

Ionics

Abstract:Ni-rich LiNi 0.6 Co 0.2 Mn 0.2 O 2 is a promising cathode material for lithium ion battery. Although the Ni-rich cathode material has high specific capacity, the increase of Ni content aggravates the interfacial side reaction at the same time, which leads to poor cycle performance and rate performance, especially at high temperature and high cutoff voltage. In this work, LiBO 2 (LBO)-coated LiNi 0.6 Co 0.2 Mn 0.2 O 2 were synthesized by a simple wet process, and the effects of LBO coating on the layered structure, particle morphology, and electrochemical behavior of the cathode materials were investigated. Electrochemical tests show that an appropriate amount of LBO coating can effectively improve the cycle performance and rate performance of the materials. Under the voltage range of 3.0–4.6 V at room temperature and 55 °C high temperature, the capacity retentions of the LiNi 0.6 Co 0.2 Mn 0.2 O 2 cathode improved from 81.0 to 91.2% and 76.9 to 85.7%, respectively, after 50 cycles at 1 C. This is because LBO has a Li–Li conductive network, the coating not only increases the diffusion rate of lithium ion, but suppresses the occurrence of harmful side reactions at the interface, thus improving the electrochemical performance of the material.

chemistry, physical,physics, condensed matter,electrochemistry