Enhanced electrochemical properties of Ni-rich LiNi0.8Co0.1Mn0.1O2 by SnO2 coating under high cutoff voltage

Liubin Song,Anxian Li,Zhongliang Xiao,Zhenzhen Chi,Zhong Cao,Huali Zhu

DOI: https://doi.org/10.1007/s11581-019-03430-6

IF: 2.961

2020-01-06

Ionics

Abstract:<p class="a-plus-plus">Extending the working voltage is an effective approach to enhance the reversible capacity of LiNi<sub class="a-plus-plus">1-x-y</sub>Co<sub class="a-plus-plus">x</sub>Mn<sub class="a-plus-plus">y</sub>O<sub class="a-plus-plus">2</sub> layered oxide cathode materials. However, the layered Ni-rich LiNi<sub class="a-plus-plus">0.8</sub>Co<sub class="a-plus-plus">0.1</sub>Mn<sub class="a-plus-plus">0.1</sub>O<sub class="a-plus-plus">2</sub> cathode suffers a severe structural instability and rapid capacity decrease during high-voltage cycling (4.6 V). In order to solve these problems, the surface coating layer of SnO<sub class="a-plus-plus">2</sub> is successfully prepared via a one-step synthesis way followed with a high temperature calcination method. The 1.0% SnO<sub class="a-plus-plus">2</sub>-modified LiNi<sub class="a-plus-plus">0.8</sub>Co<sub class="a-plus-plus">0.1</sub>Mn<sub class="a-plus-plus">0.1</sub>O<sub class="a-plus-plus">2</sub> delivers a much higher capacity retention (83.63%) compared with pristine sample (71.58%) after 100 cycles at 1 C under 4.6 V. The coating properties of SnO<sub class="a-plus-plus">2</sub>-coated LiNi<sub class="a-plus-plus">0.8</sub>Co<sub class="a-plus-plus">0.1</sub>Mn<sub class="a-plus-plus">0.1</sub>O<sub class="a-plus-plus">2</sub> are probed via X-ray diffraction, scanning electron microscope, and transmission electron microscope. Our results provide a skillful approach to obtain the promising high performance of cathode materials with both high energy density and long calendar life to satisfy the growing demands of future lithium-ion battery.</p>

chemistry, physical,physics, condensed matter,electrochemistry