Boron Doping and LiBO 2 Coating Synergistically Enhance the High-Rate Performance of LiNi 0.6 Co 0.1 Mn 0.3 O 2 Cathode Materials
Shan Gao,Baozhao Shi,Jing Liu,Lijuan Wang,Chaoyi Zhou,Cuili Guo,Jinli Zhang,Wei Li
DOI: https://doi.org/10.1021/acssuschemeng.0c09265
2021-04-03
Abstract:The nickel-rich cathode LiNi<sub>0.6</sub>Co<sub>0.1</sub>Mn<sub>0.3</sub>O<sub>2</sub> (NCM613) is a promising cathode material but has poor cycle stability, especially at a high cutoff voltage. Aiming at modulating the unit cell parameters via heteroatom dopants while providing a lithium-ion conductor coating, in this work, boron-based-modified NCM613 has been synthesized with both LiBO<sub>2</sub> coating and boron doping via a solid-state method. The optimal modified sample LBO-0.4 exhibits excellent cycle stability at room temperature (2.8–4.5 V) with a retention of 94.8% at 1 C after 100 cycles (versus 79.7% of the pristine sample LBO-0) and 70.7% at 5 C after 1000 cycles (versus a retention lower than 1% for LBO-0). The <i>D</i><sub>Li</sub><sup>+</sup> values of LBO-0.4 are significantly higher than those of LBO-0, which is attributed to the enlarged crystal lattice volume generated by the incorporation of B<sup>3+</sup> into NCM613. Combined with characterization by Ar sputtering-assisted XPS, TEM, XRD, etc., it is illustrated that LiBO<sub>2</sub> coating and B<sup>3+</sup> doping can synergistically enhance the electrochemical performance of the NCM613 at a high cutoff voltage, high temperature, and high rate. In addition, DFT calculations disclose that the boron dopant is preferential to locate in the interstice among three Ni atoms of the TM–O layer of NCM, which facilitates the formation of more amount Ni<sup>2+</sup>, leading to the improved electrochemical performance of NCM613. Such ion doping and surface coating strategy can provide useful guidance on the modification of other layered oxide cathode materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c09265?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c09265</a>.Usage amount for preparing each sample; enlarged regions for the (006)/(102) and (108)/(110) reflections; XRD refinements for LBO-0.2 and LBO-0.8; SEM images of LBO-0.2 and LBO-0.8; HRTEM image of LBO-0.8; EDS elemental mapping of Ni, Co, Mn, and O for LBO-0; boron content in the surfaces of all samples determined by XPS; initial charge and discharge curves of LBO-1.6 at 1 C and room temperature; discharge capacity at different current rates for LBO-0 and boron-modified samples (room temperature); GITT curves of LBO-0.4 and LBO-0 during the discharging process; plot of voltage against τ<sup>1/2</sup>; fragment of GITT at around 4.3 V (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c09265/suppl_file/sc0c09265_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology