High-temperature thermoelectric properties of (1-x)DyBCO − xBNT ceramics

Paitoon Boonsong,Anucha Watcharapasorn

DOI: https://doi.org/10.1080/21870764.2022.2127505

2022-10-18

Journal of Asian Ceramic Societies

Abstract:Dysprosium barium copper oxide – bismuth sodium titanate ((1- x )DyBCO− x BNT) ceramics, where x = 0−0.07 mole fraction, were successfully prepared by a solid-state reaction and sintering method. The DyBa 2 Cu 3 O 7-δ and (Bi 0.5 Na 0.5 )TiO 3 powders were separately synthesized by calcining their stoichiometric mixtures at 900°C for 4 h and 800°C for 2 h, respectively. The (1- x )DyBCO− x BNT powders were compacted into pellets and sintered at 930°C for 2 h under normal air atmosphere. Phase identification and morphology of all samples were determined using X-ray diffractometer (XRD). The quantitative phase analysis was analyzed by fitting the XRD pattern using the GSAS-II program. Scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS) was used to study microstructure and chemical composition. In all cases, the result of XRD shows that the DyBa 2 Cu 3 O 7–δ (Dy-123) was identified as the main crystalline phases, due to the good agreement between the observed and calculated patterns after Rietveld refinement. All BNT-doped DyBCO ceramics showed slightly higher density values than the undoped sample, suggesting that BNT helped improve the densification process. The sign of the Seebeck coefficient ( S ) was positive for all samples at all measured temperatures, confirming a p-type conduction mechanism. Low BNT doping improved the overall thermoelectric properties of DyBCO ceramics by affecting electrical conductivity ( σ ), Seebeck coefficient ( S ), and thermal conductivity ( κ ). The dimensionless figure of merit ( ZT=S2σT/κ ) of all samples increased with increasing temperature. The highest ZT value of 5.67 × 10 −2 was observed for the 0.97DyBCO−0.03BNT sample at 863 K.

materials science, ceramics