Energy storage performance in Dy doped Na0.425Bi0.425Ca0.15TiO3 Pb-free ceramics

Jia Dong,Mingyang Tang,Yang Li,Jingwen Lv,Kun Yu,Yi Liu,Fei Wu,Yan Yan,Gang Liu

DOI: https://doi.org/10.1016/j.ceramint.2020.07.348

IF: 5.532

2020-12-01

Ceramics International

Abstract:High capacity for the dielectric capacitors are necessary for practical applications. Additionally, dielectric capacitors should have some degree of temperature and frequency stability to allow them to adapt to environmental changes. To fulfil these requirements, Na0.425Bi0.425Ca0.15TiO3-xDy (x = 0, 2, 5, and 10 at‰) (NBCT-xDy) energy storage ceramics were produced using a traditional solid-state synthesis method. NBCT-5Dy achieved an excellent energy storage density of 2.35 J/cm3 and a good efficiency of 78.32% at 210 kV/cm. In addition, the sample was tested at 150 kV/cm under variable temperature and frequency conditions, showed a stable energy storage density of ~1.3 J/cm3 and maintains excellent efficiency at 30–150 °C and 0.2–200 Hz. Furthermore, the dielectric constant of the sample was measured at 0–40 kV/cm, and exhibited less than 2% change over this range. These results confirmed that the sample had excellent energy storage density and good stability. In the pulse discharge performance test, a high power density (46.31 MW/cm3 at 150 kV/cm) was obtained, indicating that this material has great application prospects in the pulse capacitor field in the future.

materials science, ceramics