Dysprosium doping induced effects on structural, dielectric, energy storage density, and electro-caloric response of lead-free ferroelectric barium titanate ceramics

Muhassinah Tasneem,K. Kamakshi

DOI: https://doi.org/10.1007/s10853-023-09264-y

IF: 4.5

2024-01-22

Journal of Materials Science

Abstract:This work highlights the influence of dysprosium (Dy) doping on structural, dielectric, ferroelectric, energy storage density (ESD) and the electro-caloric(EC) response of solid state synthesized Ba 1− x Dy x TiO 3 (BDT) ceramics with a composition of x varying from 0 to 0.05. The X-ray diffraction and Raman studies suggest that BDT ceramics exhibited pure perovskite tetragonal phase. Scanning electron microscopy (SEM) analysis evidences that Dy doping causes a significant reduction in grain size. The Ba 0.99 Dy 0.01 TiO 3 ceramics exhibited enhanced dielectric constant and ferroelectric polarization due to the optimum mobility of domains. The temperature-dependent dielectric studies depict that the tetragonal ferroelectric—cubic paraelectric phase transition temperature ( T c ) is shifted from 140 to 80 °C as x varies from 0 to 0.05. Further, BDT ceramics are found to be normal ferroelectric at low composition and is of relaxor type at x = 0.05. The Ba 0.99 Dy 0.01 TiO 3 ceramics exhibited optimum recoverable ESD of 278 mJ/cm 3 and an efficiency ( η ) of 67% at an electric field of 50 kV/cm. Moreover, the values of ESD and η are stable up to 10 7 cycles and at different operating temperatures ranging from RT to 70 °C. Besides, the Ba 0.99 Dy 0.01 TiO 3 ceramics demonstrated an enhanced EC effect with an adiabatic temperature change (Δ T ) 1.92 K in the vicinity of T c at a field of 50 kV/cm and an EC responsivity (Δ T / E ) 0.38 K m/MV compared to other BT based ceramics.

materials science, multidisciplinary