Effect of Dy2O3 on the Structure and Electrical Properties of (bi0.5na0.5)0.94ba0.06tio3 Lead-Free Piezoelectric Ceramics

Peng Fu,Zhijun Xu,Ruiqing Chu,Wei Li,Qian Xie,Yanjie Zhang,Qian Chen

DOI: https://doi.org/10.1016/j.jallcom.2010.08.117

IF: 6.2

2010-01-01

Journal of Alloys and Compounds

Abstract:Dy2O3 (0–0.8wt.%)-doped (Bi0.5Na0.5)0.94Ba0.06TiO3 (abbreviated as BNBT6) lead-free piezoelectric ceramics were synthesized by conventional solid-state processes. The compositional dependence of phase structure and electrical properties of the ceramics was studied. X-ray diffraction (XRD) data shows that 0.2–0.8wt.% Dy2O3 can diffuse into the lattice of BNBT6 ceramics and forms a pure perovskite phase. SEM images indicate that all the modified ceramics have a clear grain boundary and a uniformly distributed grain size, and the BNBT6 ceramics doped with appropriate Dy2O3 become denser. At room temperature, the ceramics doped with 0.6wt.% Dy2O3 have the highest piezoelectric constant (d33=170pC/N), higher mechanical quality factor (Qm=102), high relative dielectric constant (ɛr=1611) and lower dissipation factor (tanδ=0.051) at a frequency of 10kHz. The BNBT6 ceramics doped with 0.4wt.% Dy2O3 have the highest planar coupling factor (kp=0.33). Moreover, all BNBT6-x (wt.%) Dy2O3 ceramics exhibit a typical relaxor behavior with diffuse phase transition characteristics and the degree of ferroelectric relaxation behavior attains peak value at doping level of 0.4wt.%.