Preparation of fast pyrolysis carbon for NH3-SCR at low temperature: a study of experiments and DFT calculations

Juan Zhang,Guobo Li,Peng Wu,Yaping Zhang,Bingyu Li,Hongqiang Yang,Kai Shen,Sheng Wang,Feng Gong
DOI: https://doi.org/10.1007/s10853-022-07806-4
IF: 4.5
2022-10-23
Journal of Materials Science
Abstract:A series of residual carbon derived from the rapid pyrolysis of biomass was prepared and applied in the selective catalytic reduction (SCR) of NO with NH 3 . Various characterization techniques and Density Function Theory (DFT) calculations were conducted to determine the catalyst structure and reaction mechanism. Mn-loaded residual carbon from corn straw pyrolyzed at 400 °C (MnCorn4PC) exhibited the best NO x conversion of 87% at 250 °C and maintained conversion of 50% in the temperature range of 100–200 °C. The characterization results revealed that MnCorn4PC catalyst displayed higher specific surface area and more uniform dispersion of active components. It was speculated that better low-temperature redox properties, stronger surface acidity, and richer C = O species contributed to the low-temperature SCR activity of the MnCorn4PC catalyst. DFT calculation results showed that the molecules (NH 3 , NO, and O 2 ) formed a new chemical bond with the Mn site, and the highest adsorption energy of NH 3 was − 236.9 kJ/mol with the bond length of 2.09 Å. The calculation and in situ DRIFTS experiments indicated that the Langmuir–Hinshelwood (L–H) and Eley–Rideal (E–R) mechanisms simultaneously occurred on the MnCorn4PC catalyst surface, in which the adsorbed NH 3 on the Brønsted acid and Lewis acid sites reacted with NO and regenerated hydroxide as Brønsted acid for the next cycle promoting the SCR reaction process.
materials science, multidisciplinary
What problem does this paper attempt to address?