Abstract:A desirable catalyst for efficiently controlling NOx emissions often demands excellent SO2 poisoning resistance. Here, we introduced Ce to modify birnessite-MnO2 to obtain a Ce-MnO2 catalyst with excellent activity (T90 = 85 °C) for the selective catalytic reduction of NO with NH3 (NH3-SCR) at low temperatures. Compared with the MnO2 catalyst that was severely deactivated after poisoning, the Ce-MnO2 catalyst showed a significant improvement in SO2 resistance with the NO conversion slightly decreasing from 100 to 95% at 150 °C. Physicochemical characterizations combined with density functional theory calculations indicated that the sulfates formed on Mn species and Ce species played different roles in the SCR reaction. The SO32– adsorbed on the surface of the MnO2 catalyst can react with NH3 to form ammonium sulfites, leading to the deactivation of the catalyst. However, the SO42– from Ce2(SO4)3 on the sulfated Ce-MnO2 catalyst existed as new adsorption sites of NH4+, thus providing this catalyst with more acid sites. In addition, SO2 was preferentially adsorbed and oxidized on Ce species, thereby protecting the Mn active centers from sulfation and deactivation. This work reveals the mechanism of Ce in promoting SO2 resistance over birnessite-MnO2 from the perspective of sulfates.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c05697?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c05697</a>.Details of experimental section; summary of the catalytic activity of Mn–Ce catalysts for NH3-SCR at low temperatures reported in the previous literature; NH3-SCR activity and N2 selectivity of fresh catalysts; SEM and TEM images of fresh catalysts; and TG and DTG profiles of the catalysts after poisoning (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c05697/suppl_file/cs0c05697_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Comparison of Mn doped CeO2 with different exposed facets for NH3-SCR at low temperature

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Catalytic performance of CeO2-NPs and α-MnO2 mixed oxides catalysts for low-temperature NH3-SCR of NO

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Effect of different exposed crystal surface of CeO2 loading on MnO2/X catalyst for NH3-SCR reaction

Distinct effect of preparation methods on reaction efficiency of Mn-Ce/Al2O3 catalysts in low-temperature NH3-SCR

Effect of MnO2 crystal types on CeO2@MnO2 oxides catalysts for low-temperature NH3-SCR

CeO 2 Catalysts for NH 3 ‐ SCR at Low Temperatures

Mechanism and Kinetics Study on Low-Temperature NH3-SCR over Manganese–Cerium Composite Oxide Catalysts

Mn/CeO2 catalysts for SCR of NOx with NH3: comparative study on the effect of supports on low-temperature catalytic activity

Influence of Preparation Methods on the Physicochemical Properties and Catalytic Performance of MnOx-CeO2 Catalysts for NH3-SCR at Low Temperature

Mechanistic insights into the influence of preparation methods and Fe3+ doping on the low-temperature performance of MnCeO catalyst for NH3-SCR reaction

Low-temperature Selective Catalytic Reduction of NO with NH3 over MnCe Oxides Supported on TiO2 and Al2O3: A Comparative Study

Comparison of low-temperature catalytic activity and H2O/SO2 resistance of the Ce-Mn/TiO2 NH3-SCR catalysts prepared by the reverse co-precipitation, co-precipitation and impregnation method

Doping effect of rare earth metal ions Sm3+, Nd3+ and Ce4+ on denitration performance of MnO catalyst in low temperature NH3-SCR reaction

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

Mn and Fe oxides co-effect on nanopolyhedron CeO2 catalyst for NH3-SCR of NO

Mechanism of Ce-Modified Birnessite-MnO 2 in Promoting SO 2 Poisoning Resistance for Low-Temperature NH 3 -SCR

CeO2 Nanoparticle-Loaded MnO2 Nanoflowers for Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

C,N ‐modified TiO 2 ‐supported Mn–Ce–Co x ‐based catalyst for low‐temperature NH 3 ‐SCR