Abstract:Aiming to polish up the denitrification efficiency and N2 selectivity for MnCeO x catalyst at low temperature, an array of Fe3+-doped MnCeO x catalysts were synthesized through innovative approaches: the citric acid method (FeMnCeO x -CA) and CTAB-assisted template method (FeMnCeO x -ST). However, the catalysts prepared by CTAB-assisted template method (MnCeO x -ST and FeMnCeO x -ST catalysts) did not exhibit an excellent low-temperature activity compared with the catalysts made by citric acid method (MnCeO x -CA and FeMnCeO x -CA catalysts) below 300 °C. Therefore, an in-depth investigation of underlying impact of citric acid method and Fe3+ doping on MnCeO x catalyst was thoroughly implemented. We finally found that the main function of citric acid is to enhance the internal electron transfer of the catalyst by facilitating the mutual conversion between active components, particularly Mn4+/Mn3+, thereby improving the denitrification activity of FeMnCeO x -CA catalyst at low temperature. Further, the NH3-SCR performance of FeMnCeO x -CA exceed 90 % NO x conversion within 75–150 °C, and it can be reached 94 % NO x conversion at 125 °C, which was almost 10 % higher than that of MnCeO x -CA catalyst. Moreover, the N2O formation of FeMnCeO x -CA is significantly suppressed at temperatures ranging from 125-200 °C, exhibiting a higher N2 selectivity compared to MnCeO x -CA. Besides, solid solution structure of −Ce-O-Mn-O-Fe- formed after Fe3+ doping in MnCeO x catalyst strengthened surface acidity and redox ability over FeMnCeO x -CA catalyst, promoting NH3 adsorption and activation. On the other hand, the FeMnCeO x -CA catalyst exhibits the highest content of Ce3+ and Mn4+, facilitating oxygen vacancies formation and redox capacity, thereby promoting the key intermediates generation in the microscopic NH3-SCR reaction process. Finally, a reasonable Langmuir-Hinshelwood mechanism and detailed reaction pathways of NH3-SCR reaction existed on FeMnCeO x -CA catalyst were also proposed.

Distinct effect of preparation methods on reaction efficiency of Mn-Ce/Al2O3 catalysts in low-temperature NH3-SCR

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Catalytic performance of CeO2-NPs and α-MnO2 mixed oxides catalysts for low-temperature NH3-SCR of NO

Enhancement Of Scr Performance Of Monolithic Mn-Ce/Al2o3/Cordierite Catalysts By Using Modified Deposition Precipitation Method

Mechanistic insights into the influence of preparation methods and Fe3+ doping on the low-temperature performance of MnCeO catalyst for NH3-SCR reaction

Enhancing low-temperature NH3-SCR performance of Fe–Mn/CeO2 catalyst by Al2O3 modification

Comparison of Mn doped CeO2 with different exposed facets for NH3-SCR at low temperature

Doping effect of rare earth metal ions Sm3+, Nd3+ and Ce4+ on denitration performance of MnO catalyst in low temperature NH3-SCR reaction

Comparison of low-temperature catalytic activity and H2O/SO2 resistance of the Ce-Mn/TiO2 NH3-SCR catalysts prepared by the reverse co-precipitation, co-precipitation and impregnation method

Low-temperature selective catalytic reduction of NO on CeO2-CuO/Al2O3 catalysts prepared by different methods

Effect of different exposed crystal surface of CeO2 loading on MnO2/X catalyst for NH3-SCR reaction

Mesoporous MnOx-CeO2 composites for NH3-SCR: the effect of preparation methods and a third dopant

Low-temperature Selective Catalytic Reduction of NO with NH3 over MnCe Oxides Supported on TiO2 and Al2O3: A Comparative Study

Highly Selective Catalytic Reduction of NOx by MnOx–CeO2–Al2O3 Catalysts Prepared by Self-Propagating High-Temperature Synthesis

Effect of Ceria Precursor on the Physicochemical and Catalytic Properties of Mn–W/CeO2 Nanocatalysts for NH3 SCR at Low Temperature

Mechanism and Kinetics Study on Low-Temperature NH3-SCR over Manganese–Cerium Composite Oxide Catalysts

Low-temperature selective catalytic reduction of NO with NH3 over Mn–Ce–Ox/TiO2: a comparison between catalyst preparation methods

Effect of MnO2 crystal types on CeO2@MnO2 oxides catalysts for low-temperature NH3-SCR

Highly Dispersed Surface Active Species of Mn/Ce/TiW Catalysts for High Performance at Low Temperature NH3-SCR

Investigation of long-term anti-sulfur and deactivation mechanism of monolithic Mn-Fe-Ce/Al 2 O 3 catalysts for NH 3 -SCR: Changes in physicochemical and adsorption properties

Improvement of Activity and SO2 Tolerance of Sn-Modified MnOx–CeO2 Catalysts for NH3-SCR at Low Temperatures