Abstract:A range of Fe-Cr-Ni alloys are used in nuclear power plants due to their high mechanical strength and corrosion resistance. As a major component of these alloys, Ni contributes to the formation of austenite microstructures. In many nuclear reactor applications the alloys are exposed to ionizing radiation (g-rays) that can continuously decompose water to a range of highly redox active species (such as •OH, H2O2, O2). The change in water chemistry induced by radiation can affect both the general and localized corrosion behaviour of these alloys. In particular, its influence on the susceptibility of an alloy to localized corrosion such as crevice and stress corrosion cracking (SCC) are important for assessment of reactor component aging. As well, corrosion products that dissolve into the reactor coolant can be transported to the reactor core where they can be neutron activated. This can create a radiological hazard for reactor maintenance personnel. Thus, quantifying the rate of general corrosion and the corrosion product transport in a reactor are important safety, operation and maintenance issues. It has been well established that the type of oxide that forms on a surface is a critical factor in determining both general and localized corrosion behaviour. Both alloy composition and water chemistry affect the type of oxide that forms. Systematic studies that examine the effect of alloy composition on corrosion are rare and those available have been conducted mostly from a metallurgical perspective. There are even fewer studies that examine the combined effects of alloy composition and corrosion environment. A fundamental understanding of the mechanism by which the Fe to Ni ratio in a steel alloy influences the corrosion rate in different environments will provide valuable information that can be used for alloy selection and usage. We have investigated the effect of the Fe to Ni ratio of alloy on oxide formation and growth kinetics. For this study, customized steel alloys with different Ni contents and constant Cr content (18 ± 1 %) were prepared. The Ni content ranged from 15 to 25 wt.%, within the range between AISI 316L and Alloy 800 (Fig. 1). The corrosion kinetics was investigated using a combination of coupon corrosion tests and electrochemical measurements. These measurements were augmented by oxide surface and depth analyses using several spectroscopic and imaging techniques, and by post-test solution analyses for dissolved metal loss. We found that the oxide formed at pH 10.6 and 80 °C has a graded layer structure, consisting of a mixed spinel oxide (FeCr2O4/Fe3O4/NiFe2O4) as an inner layer and Ni(OH)2 as an outer layer. The increase in Ni content from 15 to 25 wt.% does not affect the inner layer but increases the thickness of the Ni(OH)2 layer. The increase in Ni content also decreases the total amount of dissolved metal loss. Gamma-irradiation of the corroding system increases the corrosion potential on these alloys. Correspondingly, gamma-radiation accelerates the formation of passive oxide layers and decreases the overall rate of metal dissolution. The observed kinetics of oxide growth and metal dissolution can be explained by the competition kinetics of oxide growth and dissolution for oxidized metals. Figure 1

Corrosion Behavior of Low-Temperature Nickel and Iron Aluminized Martensitic Stainless Steel Substrates with Different Surface Roughness in Acidic Medium

Influence of Ni Addition on Corrosion Performance of Medium-temperature Filler Metal with Low Cu Content for Al Brazed Joints

Microstructural Investigation and Oxidation Performance of Nickel-Based Superalloys

Microstructure and Corrosion Study on Friction Surfaced Aluminum Alloy Coatings over Mild Steel

Hot Corrosion and Oxidation Behavior of Pt–Aluminide and Pt–Rh–Aluminide Coatings Applied on Nickle-Base and Cobalt-Base Substrates

Oxidation Behavior of Arc-Sprayed FeMnCrAl/Cr3C2–Ni9Al Coatings Deposited on Low-Carbon Steel Substrates

Corrosion behaviour of iron and nickel aluminide coatings under the synergistic effect of NaCl and water vapour

Corrosion Behavior of Ni-P-Nano-Al2o3 Composite Coating in the Presence of Anionic and Cationic Surfactants

Effect of Substrate Roughness on Oxidation Resistance of an Aluminized Ni-Base Superalloy

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

Corrosion Resistance, Composition, and Stratification of Passive Films: Ni-22Cr and Ni-22Cr-6Mo Alloys Passivated and Exposure Aged in Acidic Chloride Solutions

Corrosion behavior of multi-layer friction surfaced structure from dissimilar aluminum alloys

The effect of surface preparation on high temperature oxidation of Ni, Cu and Ni-Cu alloy

Lower temperature aluminizing and its effect on improving corrosion resistance of iron treated by surface mechanical attrition treatment

Effects of Nickel on the Oxide/Metal Interface Morphology and Oxidation Rate During High-Temperature Oxidation of Fe–Cu–Ni Alloys

High-Temperature Corrosion of APS- and HVOF-Coated Nickel-Based Super Alloy under Air Oxidation and Melted Salt Domains

Characterization of microstructure, grain distribution, and tribocorrosion properties of NiTi-based alloy

Corrosion behavior of laser powder bed fusion manufactured nickel-free stainless steels in high-temperature water

Long-Term Testing of WC–Ni–Fe Coating as an Inert Anode in a Low-Temperature Electrolyte for Aluminum Production

Electrochemical Corrosion Behavior of Nickel-Coated Carbon Fiber Materials in Various Electrolytic Media

Effect of Nickel Content on the Corrosion Behaviour of Stainless Steel at 80 °C