Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

Preparation of liquid polycarbosilane containing vinyl ether group and its rapid curing through thiol‐ene click reaction

Preparation of SiC ceramic fiber from a photosensitive polycarbosilane

Digital light processing of SiC ceramic from allylhydridopolycarbosilane with limited acrylate monomers

A novel high reactive initiator system of vinyl‐substituted hydridopolycarbosilane (VHPCS) for lower curing temperature and higher ceramic yields

Preparation of functional ethoxysilane-containing polyethylene through ethylene coordination copolymerization catalyzed by iminopyrrolide vanadium complex

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Allyl-Substituted Hydridopolycarbosilane with Low Curing Temperature and High Ceramic Yield under a Redox Initiation System

Curing reactions of liquid hydridopolycarbosilanes with vinyl or allyl groups

Polymerization of polycarbosilanes in high internal phase emulsions for the synthesis of macroporous silicon carbide catalysts (polyHIPE-SiC)

A New SiC Precursor with High Ceramic Yield: Synthesis and Characterization of CHxMeSiH2‐containing Poly(methylsilane‐carbosilane)

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Preparation and Characterization of Polyborosiloxanes and Their Blends with Phenolic Resin As Shapeable Ceramic Precursors

Evaluation of Poly(methylsilane‐carbosilane) Synthesized from Methyl‐dichlorosilane and Chloromethyldichloromethylsilane As a Precursor for SiC

Additive manufacturing of ceramics from preceramic polymers: A versatile stereolithographic approach assisted by thiol-ene click chemistry

Influence of polycarbosilane composition on the properties of SiC/SiC composite fabricated by precursor infiltration and pyrolysis process

Polymethylsilane As A Precursor to High-Purity Silicon-Carbide

Investigation of curing behavior and mechanical properties of SiC ceramics prepared by vat photopolymerization combined with pressureless liquid-phase sintering using Al 2 O 3 -coated SiC powder

Synthesis and characteristics of polycarbomethylsilane via a one-pot approach

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

One-step synthesis of epoxy-based silicon prepolymers and its application in UV-curable coating

Facile synthesis of a carbon-rich SiAlCN precursor and investigation of its structural evolution during the polymer-ceramic conversion process