Hydrogen diffusion and hydrogen embrittlement failure behavior of AH36 marine steel subjected to high heat input welding

Dazheng Zhang,Changzhi Cui,Weijuan Li,Jiakai Xu
DOI: https://doi.org/10.1002/srin.202200539
IF: 2.1258
2022-10-14
steel research international
Abstract:AH36 marine steel processed through high heat input welding was subjected to microstructural characterization, hydrogen permeation test, internal friction test, and slow strain rate tensile test to reveal its hydrogen diffusion and hydrogen embrittlement failure behaviors. Compared with the base metal, the coarse‐grained heat‐affected zone (CGHAZ) exhibited a significantly coarsened microstructure and decreased hydrogen trap density, resulting in a high hydrogen diffusion coefficient and short hydrogen permeation time. The presence of hydrogen yielded a hydrogen‐induced Snoek internal friction peak and promoted the movement of the Snoek–Kê–Köster internal friction peak to the low‐temperature region. Additionally, B and Kê peaks, which were not found in the base metal, appeared in the CGHAZ. With increasing hydrogen content, the plastic loss and brittle fracture of the AH36 marine steel became increasingly significant, and the hydrogen embrittlement sensitivity of the heat‐affected zone increased compared to that of the base metal. The discontinuous yield phenomenon gradually disappeared under slow strain rate tension owing to the weak pinning effect of the Cottrell atmosphere on mobile dislocations. This article is protected by copyright. All rights reserved.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?