Hydrogen Embrittlement Susceptibility of Gas Metal Arc Welded Joints from a High‐Strength Low‐Alloy Steel Grade S690QL

Martin Christ,Xiaofei Guo,Rahul Sharma,Tianyi Li,Wolfgang Bleck,Uwe Reisgen

DOI: https://doi.org/10.1002/srin.202000131

IF: 2.1258

2020-04-27

steel research international

Abstract:<p>This study investigated the hydrogen embrittlement (HE) susceptibility of base material and gas metal arc welds from a high‐strength low‐alloy steel grade S690QL by slow strain rate test (SSRT) with in‐situ hydrogen charging. In order to investigate the influence of welding process parameters on the HE susceptibility of welded joints, gas metal arc welds in multilayer technique with two different heat inputs were carried out. The results revealed a considerable loss of fracture elongation for all hydrogen‐charged specimens when compared to the uncharged reference conditions. If the higher heat input is chosen, the required minimum yield strength in the weld metal has not been achieved. It is remarkable that this weld metal also revealed increased HE susceptibility as measured by the relative elongation loss, despite its higher ductility associated with the lower strength level. In combination with hydrogen measurements and fracture surface analysis, the crack propagation mechanisms and related HE mechanisms were intensively discussed.</p><p>This article is protected by copyright. All rights reserved.</p>

metallurgy & metallurgical engineering