Abstract:Purpose This study aims to comprehensively investigate the mixed-mode fracture behavior and mechanical properties of selective laser sintering (SLS) polyamide 12 (PA12) components, considering different build orientations and layer thicknesses. The primary objectives include the following. Conducting mixed-mode fracture and mechanical analyses on SLS PA12 parts. Investigating the influence of build orientation and layer thickness on the mechanical properties of SLS-printed components. Examining the fracture mechanisms of SLS-produced Arcan fracture and tensile specimens through experimental methods and finite element analyses. Design/methodology/approach The research used a combination of experimental techniques and numerical analyses. Tensile and Arcan fracture specimens were fabricated using the SLS process with varying build orientations (X, X–Y, Z) and layer thicknesses (0.1 mm, 0.2 mm). Mechanical properties, including tensile strength, modulus of elasticity and critical stress intensity factor, were quantified through experimental testing. Mixed-mode fracture tests were conducted using a specialized fixture, and finite element analyses using the J-integral method were performed to calculate fracture toughness. Scanning electron microscopy (SEM) was used for detailed morphological analysis of fractured surfaces. Findings The investigation revealed that the highest tensile properties were achieved in samples fabricated horizontally in the X orientation with a layer thickness of 0.1 mm. Additionally, parts manufactured with a layer thickness of 0.2 mm exhibited favorable mixed-mode fracture behavior. The results emphasize the significance of build orientation and layer thickness in influencing mechanical properties and fracture behavior. SEM analysis provided valuable insights into the failure mechanisms of SLS-produced PA12 components. Originality/value This study contributes to the field of additive manufacturing by providing a comprehensive analysis of the mixed-mode fracture behavior and mechanical properties of SLS-produced PA12 components. The investigation offers novel insights into the influence of build orientation and layer thickness on the performance of such components. The combination of experimental testing, numerical analyses and SEM morphological observations enhances the understanding of fracture behavior in additive manufacturing processes. The findings contribute to optimizing the design and manufacturing of high-quality PA12 components using SLS technology.

Mixed-mode load bearing estimation of the cracked additively manufactured materials using stress/strain-based models

Mixed-mode fracture prediction of acrylonitrile butadiene styrene material fabricated via fused deposition modeling

Experimental and theoretical investigation of the influence of post-curing on mixed mode fracture properties of 3d-printed polymer samples

Non-local and local criteria based on the extended finite element method (XFEM) for fracture simulation of anisotropic 3D-printed polymeric components

Failure Analysis and Mechanical Characterization of 3D Printed ABS With Respect to Layer Thickness and Orientation

An Investigation of Tensile, Fatigue, and Fracture Behavior of 3D-Printed Polymers

Role of Dynamic Response in Inclined Transverse Crack Inspection for 3D-Printed Polymeric Beam with Metal Stiffener

Computing the bond strength of 3D printed polylactic acid scaffolds in mode I and II using experimental tests, finite element method and cohesive zone modeling

Modelling the Variability and the Anisotropic Behaviour of Crack Growth in SLM Ti-6Al-4V

The Influence of Microstructural Arrangement on the Failure Characteristics of 3D-Printed Polymers: Exploring Damage Behaviour in Acrylonitrile Butadiene Styrene

Exploring mixed-mode fracture behavior and mechanical properties of selective laser sintered polyamide 12 components

Predicting failure modes of 3D-printed multi-material polymer sandwich structures from process parameters

The numerical model of additive manufactured carbon fiber reinforced polymer under mechanical loading

Research on Crack Propagation of 3D Printed Material with Complex Cracks Based on the Phase-Field Fracture Model

Material characterization and micro-damage detection of additive manufactured poly-lactic-acid products using material extrusion-based technique

Mode I/II cracking behavior of additively manufactured interpenetrating phase composites (IPC), an experimental and theoretical study

Progressive Damage and Crack Propagation Analysis of Composite-Patched Aluminum Plate with 3D Inclined Crack under Fatigue Loading

Modeling the fracture behavior of 3D-printed PLA as a laminate composite: Influence of printing parameters on failure and mechanical properties

Effects of Anisotropic Microstructure and Load Ratio on Fatigue Crack Propagation Rate in Additively Manufactured Ti-6Al-4V Alloy

Effects of Anisotropic Mechanical Behavior on Nominal Moment Capability of 3D Printed Concrete Beam with Reinforcement

Damage modeling in additive manufacturing processes for metals