Abstract:Through multimaterial 3D printing, a remarkable up to 14% increase in tensile strength is achieved, while salt remelting further enhances structural rigidity. This study comprehensively evaluates mechanical and wear properties, utilizing scanning electron microscope images for in‐depth morphological analysis. This showcases the potential of 3D printing in tailoring material properties for advanced applications. 3D printing has witnessed a remarkable surge in popularity due to its flexibility in design and adaptability as a manufacturing technique to nearly each industrial area. This study focuses on harnessing the technological versatility of 3D printing by utilizing both standard poly lactic acid (PLA) and copper powder‐doped PLA to fabricate intricate structures through a layer‐by‐layer additive manufacturing process. The other innovation introduced here lies in the postprocessing step, which involves salt remelting. The mechanical properties of 3D‐printed standard test specimens undergo comprehensive assessment, encompassing bending and tensile evaluations, hardness measurements, density assessments, dimensional stability analyses, and wear resistance examinations. Utilizing copper powder‐doped PLA for the initial and final layers in XYZ‐oriented prints enables multimaterial printing, resulting in an ≈14% increase in tensile strength. Subsequently, subjecting this multimaterial composite to salt remelting elevates the strength enhancement to ≈16%, accompanied by a significant boost in rigidity by reducing voids in cross‐sectional area. In addition, scanning electron microscope images are captured, allowing for a detailed morphological analysis, which is then correlated with the findings of the various tests performed. This research unveils the potential of 3D printing technology in crafting materials with tailored mechanical properties, advancing its applicability in numerous industrial sectors.

Material characterization and micro-damage detection of additive manufactured poly-lactic-acid products using material extrusion-based technique

An Investigation of Tensile, Fatigue, and Fracture Behavior of 3D-Printed Polymers

Evolution of microstructure and thermo‐mechanical attributes of fiber reinforced polyamide during fused deposition modeling 3D printing: A comprehensive characterization study

Investigating the Integrity and Failure Characteristics of Deteriorated Polymeric 3D-Printed Components as Candidates for Structural and Construction Applications

A Comparative Investigation of the Reliability of Biodegradable Components Produced through Additive Manufacturing Technology

Carbon Fibre Damage During 3D Printing of Polymer Matrix Laminates Using the FDM Process

The Influence of Microstructural Arrangement on the Failure Characteristics of 3D-Printed Polymers: Exploring Damage Behaviour in Acrylonitrile Butadiene Styrene

Failure Analysis and Mechanical Characterization of 3D Printed ABS With Respect to Layer Thickness and Orientation

Analyzing the Influence of Multimaterial 3D Printing and Postprocessing on Mechanical and Tribological Characteristics

Electro-Mechanical Characterisation and Damage Monitoring by Acoustic Emission of 3D-Printed CB/PLA

Characterization of 3D-printed PLA parts with different raster orientations and printing speeds

Improving the fracture toughness of 3D printed thermoplastic polymers by fused deposition modeling

Characterisation of Mechanical Behaviour of 3D Printed Rock-Like Material with Digital Image Correlation

Mechanical Performance of 3D Printed Polylactide During Degradation

Modeling the fracture behavior of 3D-printed PLA as a laminate composite: Influence of printing parameters on failure and mechanical properties

Experimental Study of the Tensile Behavior of Structures Obtained by FDM 3D Printing Process

Experimental Analysis and Design of 3D-Printed Polymer Elliptical Tubes in Compression

Effect of Degradation of Polylactic Acid (PLA) on Dynamic Mechanical Response of 3D Printed Lattice Structures

Microscopic analysis of mechanical anisotropy and damage evolution of 3D printed rock-like samples under uniaxial compressive tests

Impact of processing defects on microstructure, surface quality, and tribological performance in 3D printed polymers

Experimental monitoring and modeling of fatigue damage for 3D-printed polymeric beams under irregular loading