Abstract:The effect of nano-CaO content on the microstructure, mechanical properties, and in vitro degradation performance of extruded Mg-1Zn alloys was investigated to enhance the strength and corrosion resistance of biodegradable materials for medical implants. The results showed that the addition of CaO nanoparticles effectively refined the size of dynamic recrystallization grains in the extruded composites. During the extrusion process, Ca 2 Mg 6 Zn 3 and Mg 2 Ca phases precipitated in the Mg-1Zn-0.5CaO and Mg-1Zn-1CaO composites, respectively. As the CaO content increased, the basal texture strength was elevated from 3.97 for the Mg-1Zn alloy to 12.05 for the Mg-1Zn-1CaO composite. Benefiting from the combined mechanisms of grain refinement, dislocation strengthening, and precipitation strengthening, the yield strength of the materials was fortified with an increase in CaO content. During the short immersion time, the matrix of the extruded Mg-1Zn-0.5CaO composite was preferentially corroded, resulting in the formation of a dense corrosion product layer that impeded the transport of ions in the electrolyte solution, thereby exhibiting the lowest annual corrosion rate. With an increase in the immersion time, galvanic corrosion destroyed the protective film, leading to a slightly higher corrosion rate in the extruded Mg-1Zn-0.5CaO composite compared to the Mg-1Zn alloy. The substantial nano-Mg 2 Ca phase particles were preferentially degraded, causing severe pitting corrosion in the extruded Mg-1Zn-1CaO composite, which exhibited the highest degradation rate. The extruded Mg-1Zn-0.5CaO composite exhibited superior overall properties; its yield strength, elongation, and annual corrosion rate after immersion (21 d) were 334.9 MPa, 8.9 %, and 1.06 mm/y, respectively.

Microstructure, mechanical properties and corrosion fatigue behaviour of biodegradable Mg–Zn–Y–Nd alloy prepared by double extrusion

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Effect of extrusion process on the mechanical and in vitro degradation performance of a biomedical Mg-Zn-Y-Nd alloy

A newly developed Mg-Zn-Gd-Mn-Sr alloy for degradable implant applications: Influence of extrusion temperature on microstructure, mechanical properties and in vitro corrosion behavior

Effects of extrusion parameters on the microstructure, corrosion resistance, and mechanical properties of biodegradable Mg–Zn–Gd–Y–Zr alloy

Optimization of Microstructure and Mechanical Property of a Mg-Zn-Y-Nd Alloy by Extrusion Process

Optimizing Mechanical Property and Cytocompatibility of the Biodegradable Mg-Zn-Y-Nd Alloy by Hot Extrusion and Heat Treatment

Microstructural Characteristics and Mechanical Properties of the Hot Extruded Mg-Zn-Y-Nd Alloys

Effect of extrusion process on microstructure and mechanical and corrosion properties of biodegradable Mg−5Zn−1.5Y magnesium alloy

Effect of original grain size on microstructure and properties of extruded Mg-2Zn-0.2Mn biomedical alloy

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Effect of Extrusion on Mechanical Property, Corrosion Behavior, and In Vitro Biocompatibility of the As-Cast Mg-Zn-Y-Sr Alloy

Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials

Microstructure, Texture, Mechanical Properties, and Corrosion Behavior of Biodegradable Zn-0.2Mg Alloy Processed by Multi-Directional Forging

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

An in vitro and in vivo study of biodegradable Zn–Cu–Li alloy with high strength and ductility fabricated by hot extrusion combined with room-temperature ECAP

The Effect of Heat Treatment and Extrusion on Microstructure and Properties of Medical Mg-1Mn-2Zn Alloy

Effect of Hot Extrusion on Microstructure, Texture, and Mechanical Properties of Mg-Zn-Mn-0.5Ca Alloy

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal