Abstract:Fatigue strength improvement of mechanical components is one of the most challenging problems in engineering. One of the known ways to improve fatigue life is by using the shot peening process. However, it is complex to define the optimum shot peening parameters to different materials due to the interaction of several variables. This work aimed to investigate the effect of the complex interaction of surface roughness, the residual stresses induced, the stability of the compressive residual stresses during fatigue cycles, and the work hardening of the surface layers induced by the shot peening process on the fatigue behavior of AA 6005-T6 aluminum alloy at room temperature. Rotating bending fatigue tests () were carried out on specimens in the as-machined, as-ground, and shot peened with two different intensities (0.006 N and 0.007 A) conditions. The results indicate that both shot peening conditions were capable of improving fatigue life compared to as-machined condition. However, the best fatigue behavior was achieved for the more severe condition (0.007 A), which was capable of shifting the crack source to beneath the surface, as observed through scanning electron microscopy. Although the maximum compressive residual stress was higher for the more severe condition, it was observed a relaxation of the compressive residual stresses after rotating bending fatigue cycles. It was demonstrated that, despite the stress relaxation and the surface damage induced by shot peening, the work hardening generated by the more severe condition nearby the surface was determinant to the efficiency of the process.

Improved fatigue strength of Cr-electroplated 7075-T6 Al alloy by micro-shot peening

Anti-fatigue strengthening mechanism of conventional shot peening and micro-shot peening on bare and micro-arc oxidation coated 6082-T6 aluminum alloy

Microstructure and residual stress modulation of 7075 aluminum alloy for improving fatigue performance by laser shock peening

Investigation of residual stress, stress relaxation and work hardening effects induced by shot peening on the fatigue life of AA 6005-T6 aluminum alloy

Enhanced fatigue strength of 2A02 aluminum alloy via micro laser shock peening

Surface Nanocrystallization Induced by Shot Peening and Its Effect on Corrosion Resistance of 6061 Aluminum Alloy

Surface characteristics and stress corrosion behavior of AA 7075-T6 aluminum alloys after different shot peening processes

Cumulative Fatigue damage of AA7075-T6 under Shot Peening and Ultrasonic Surface Treatments

A study of shot peening and spinning rolling on fatigue of Al 7075 alloy samples

Effect of Shot Peening on Surface Characteristics and Fatigue Properties of T5-Treated ZK60 Alloy

Surface Characteristics and High Cycle Fatigue Performance of Shot Peened Magnesium Alloy ZK60

Effect of laser shock peening on the high-temperature fatigue performance of 7075 aluminum alloy

Fatigue life improvement by shot peening for pre‐fatigue tested carburized steel

Effect of Micro-Shot Peening on the Fatigue Performance of AISI 304 Stainless Steel

Application of shot peening to improve fatigue properties via enhancement of precipitation response in high-strength Al-Cu-Li alloys

Grain refinement and fatigue strengthening mechanisms in as-extruded Mg-6Zn-0.5Zr and Mg-10Gd-3Y-0.5Zr magnesium alloys by shot peening

Relationship between Stress State and Microstructure of 7B04 Aluminum Alloy Surface Fatigue Properties by Laser Shock Peening Improvement

Effects of laser shock peening on fatigue crack growth rate and fracture properties of AA2524 aluminum alloy

Enhancing plain fatigue strength in aluminum alloys through shot peening: Experimental investigations and a strain energy density interpretation

Investigation on Improving the Fretting Wear Properties of Ti6Al4V Alloy via Micro-shot Peening to Produce Surface Asperities and Surface Hardening Layer

Effect of surface high density twin microstructure induced by shot peening on the fatigue behavior of Ti-6Al-4V