Microstructure and residual stress modulation of 7075 aluminum alloy for improving fatigue performance by laser shock peening

Xinlei Pan,Liucheng Zhou,Chenxi Wang,Kun Yu,Yiqi Zhu,Min Yi,Lingfeng Wang,Shifeng Wen,Weifeng He,Xiaoqing Liang
DOI: https://doi.org/10.1016/j.ijmachtools.2022.103979
IF: 10.331
2022-11-29
International Journal of Machine Tools and Manufacture
Abstract:Laser shock peening (LSP) is an advanced surface-strengthening technology that improves the anti-fatigue performance of metallic components. However, there is a significant barrier to the application of thin-walled components because the high-energy laser causes deformation and nonuniformity of compressive residual stress, thereby reducing fatigue performance. In this study, an LSP technology based on a low-pulse-energy laser was developed. We applied it to a thin-walled AA7075 aluminium alloy specimen (∼4 mm thickness) and achieved an improvement in the high-cycle fatigue limit of 20.4 and 37.0% for the smooth and pre-cracked fatigue specimens, respectively, in the absence of deformation. It was discovered that the enhanced dynamic nanoscale precipitation and dislocation multiplication effects of the high-pressure shock wave contribute to microstructure stability under cyclic loading, resulting in high compressive residual stress stability. Moreover, the unique heterogeneous grain structure on the surface layer subjected to LSP at low pulse energy effectively restrains crack initiation and propagation. Because these findings apply to a wide range of alloys, the current results create new avenues for improving the fatigue performance of thin-walled components.
engineering, mechanical, manufacturing
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is: how to improve the fatigue performance of 7075 aluminum alloy thin - walled parts through low - pulse - energy laser shock peening (LSP) technology while avoiding the deformation and non - uniform residual stress problems caused by high - energy lasers. Specifically, the research aims to develop an LSP technology based on low - pulse - energy lasers to increase the high - cycle fatigue limit of 7075 aluminum alloy thin - walled specimens without causing deformation. The study found that low - pulse - energy LSP can significantly improve the fatigue performance of the material, which is mainly attributed to the formation of dynamic nano - precipitates and heterogeneous grain structures. These structures help maintain the microstructural stability and the stability of high compressive residual stress under cyclic loading. ### Background of the Paper - **Fatigue Performance**: The fatigue performance of mechanical components is a key factor in determining their reliability and sustainability. However, most components that experience alternating strains and stresses during operation will suffer permanent damage or catastrophic fatigue fractures after a certain service life. - **Surface Strengthening Technology**: Since most fatigue cracks originate from the workpiece surface, surface strengthening technology has become a feasible and cost - effective method to increase the value of industrial components, especially for some complex - shaped components that are difficult to detect. - **Laser Shock Peening (LSP)**: The LSP technology significantly improves the mechanical properties of metal components by introducing high - amplitude compressive residual stress and a finer microstructure. However, high - energy lasers may cause deformation of thin - walled components and non - uniform distribution of compressive residual stress, thereby reducing the fatigue performance. ### Research Methods - **Experimental Materials**: AA7075 aluminum alloy plates with a thickness of 4 mm were used. - **LSP Process**: An Nd - YAG laser with a wavelength of 1064 nm and a pulse duration of 20 ns was used. The laser power densities were 1.8, 2.7, and 3.5 GW/cm², and the corresponding peak pressures were 4685, 5738, and 6533 MPa, respectively. - **Performance Testing**: Residual stress was measured by X - ray diffraction method, surface hardness was measured using a Vickers micro - hardness tester, and high - cycle fatigue tests were carried out to evaluate the fatigue performance. ### Main Findings - **Improvement in Fatigue Performance**: After low - pulse - energy LSP treatment, the high - cycle fatigue limits of smooth and pre - cracked fatigue specimens increased by 20.4% and 37.0%, respectively. - **Microstructural Changes**: The effects of dynamic nano - precipitation and dislocation multiplication are enhanced under the action of high - pressure shock waves, which helps maintain the microstructural stability and the stability of high compressive residual stress under cyclic loading. - **Heterogeneous Grain Structure**: A unique heterogeneous grain structure was formed in the surface layer after LSP treatment, which effectively inhibits the initiation and propagation of cracks. ### Conclusion This study demonstrates the potential of low - pulse - energy LSP technology in improving the fatigue performance of 7075 aluminum alloy thin - walled parts, providing a new theoretical and technological basis for the wider application of LSP technology.