Investigation on Improving the Fretting Wear Properties of Ti6Al4V Alloy via Micro-shot Peening to Produce Surface Asperities and Surface Hardening Layer

Mingyuan Zhang,Xu Zhao,Yingjuan Ma,Xianzheng Zhang,Cunkuan Zhu

DOI: https://doi.org/10.1007/s11665-024-09332-7

IF: 2.3

2024-03-20

Journal of Materials Engineering and Performance

Abstract:This study aims to evaluate the effect of micro-shot peening (MSP) on the fretting wear behavior of Ti6Al4V. For this purpose, Ti6Al4V alloy specimens employed in this study were subjected to MSP treatment using three injection air pressures (0.2, 0.4 and 0.6 MPa). The surface morphologies, microstructure and hardness of the treated specimens were then observed and measured. Following this, the fretting wear tests with three different sliding displacements were conducted, and parameters such as fretting hysteresis loops, wear morphologies, dissipated energy and wear volume were obtained and evaluated. The test results indicate that the surface structure of the specimens experienced severe plastic deformation, leading to surface grain refinement and increased surface hardness. Moreover, an increase in injection air pressure was found to lead to higher surface roughness and hardness. It was found that the anti-fretting wear ability of Ti6Al4V was effectively improved after MSP treatment. In cases where the sliding displacement was small, the fretting wear behavior was primarily influenced by surface asperities, and a rougher surface proved helpful in impeding fretting wear by limiting the local relative slip on contact surfaces. As the sliding displacement increased, anti-fretting wear ability will be improved at a moderate injection air pressure, thus generating a good combination between the hardness and the toughness of the surface material.

materials science, multidisciplinary