Abstract:The Ni based catalysts have been considered as potential candidates for the CO2 methanation owing to the low cost. However, the poor low-temperature catalytic activities limit their large-scale industrial application. In order to address this challenge, a series of Co-Ni bimetal doped ordered mesoporous Al2O3 materials have been designed and fabricated via the one-pot evaporation induced self-assembly strategy and employed as the catalysts for CO2 methanation. It is found that the large specific surface areas (up to 260.0 m(2/)g), big pore volumes (up to 0.59 cm(3)/g), and narrow pore size distributions of these catalysts have been successfully retained after 700 degrees C calcination. The Co and Ni species are homogenously distributed among the Al2O3 matrix due to the unique advantage of the one-pot synthesis strategy. The strong interaction between metal and mesoporous framework have been formed and the severely thermal sintering of the metallic Co-Ni active centers can be successfully inhibited during the processes of catalyst reduction and 50 h CO2 methanation reaction. More importantly, the synergistic effect between Co and Ni can greatly enhance the low-temperature catalytic activity by coordinating the activation of H-2 and CO2, prominently decreasing the activation energy toward CO2 methanation. As a result, their low-temperature activities are evidently promoted. Furthermore, the effect of the Co/(Co + Ni) molar percentage ratio on the catalytic property has been also systematically investigated over these catalysts. It is found that only the catalyst with appropriate ratio (20.0%) behaves the optimum catalytic performances. Therefore, the current Co-Ni based ordered mesoporous materials promise potential catalysts for CO2 methanation. (C) 2018 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Modifying Spinel Precursors for Highly Active and Stable Ni‐based CO2 Methanation Catalysts

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

High-Stability ZnAl2O4 Spinel-Supported Nickel Catalyst for High-Temperature Syngas Methanation

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

CO2 Methanation: Nickel–Alumina Catalyst Prepared by Solid-State Combustion

NixAl1O2-δ Mesoporous Catalysts for Dry Reforming of Methane: the Special Role of NiAl2O4 Spinel Phase and Its Reaction Mechanism

Mesoporous Manganese-Cobalt Oxide Spinel Catalysts for CO2 Hydrogenation to Methanol

An Al2O3-supported NiFe bimetallic catalyst derived from hydrotalcite precursors for efficient CO2 methanation

Highly active Ni/Al2O3 catalyst for CO2 methanation by the decomposition of Ni-MOF@Al2O3 precursor via cold plasma

Ni Based Catalysts Supported on Ce Modified MgAl Spinel Supports for High Temperature Syngas Methanation

Dry reforming of methane over nickel catalysts supported on magnesium aluminate spinels

An Active Manganese Promoted Ni/Al2O3 Catalyst for Low Temperature CO2 Methanation

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Synthesis of nanosized mesoporous Co–Al spinel and its application as solid base catalyst

Ni-Mn catalysts on silica-modified alumina for CO2 methanation

Bound-state Ni species — a superior form in Ni-based catalyst for CH4/CO2 reforming

MoOx-Doped Ordered Mesoporous Ni/Al2O3 Catalyst for CO Methanation

Ni-based catalysts supported on MgAl<sub>2</sub>O<sub>4</sub> with different properties for combined steam and CO<sub>2</sub> reforming of methane

Cobalt promoted Ni/MgAl2O4 catalyst in lean methane catalytic oxidation

Facile preparation of a Ni/MgAl2O4 catalyst with high surface area: enhancement in activity and stability for CO methanation

High-performance Nano-Structured Ni Based Catalysts for High-Temperature CO2CH4 Reforming—greenhouse Gases to Syngas