Abstract:The hydrogenation of CO 2 enables the production of high-value fuels and chemicals, contributing to a sustainable and environmentally friendly energy transition. Currently, for CO 2 hydrogenation to methanol reaction, either increasing CO 2 conversion or improving the selectivity of methanol under keeping high CO 2 conversion is challenging. A new loaded catalyst with Cu nanoparticles (NPs) dispersed on amorphous MoO x and Li 2 CO 3 as promoter (labelled as Li-Cu/MoO x ) was constructed by an in-situ dispersion and alkali metal promotion stepwise regulation strategy. At 260°C and 5 MPa, the as-designed catalyst exhibited satisfactory catalytic performance, with the CO 2 conversion of 13.4% and the methanol selectivity of 88.8%. The methanol selectivity of the Li-Cu/MoO x catalyst is higher than all Cu-based catalysts reported in the literature under the conditions of CO 2 conversion higher than 10% and reaction pressure lower than 8 MPa in fixed-bed reactor. Furthermore, the Li-Cu/MoO x catalyst showed excellent thermal stability. It was found that the in-situ dispersion step enables a higher dispersion of Cu NPs and the production of amorphous MoO x support, resulting in more Cu-support interfaces which increased the number of active sites of the catalyst. The high methanol selectivity was attributed to alkali metal promotion step which increased the Mo 4+ content in the MoO x , leading to a change in the types of active sites. In addition, the strong metal-support interaction (SMSI) in the catalyst was responsible for the high thermal stability. This strategy is also potential for designing other highly efficient catalysts.

Mesoporous Manganese-Cobalt Oxide Spinel Catalysts for CO2 Hydrogenation to Methanol

High-performance Hybrid Oxide Catalyst of Manganese and Cobalt for Low-Pressure Methanol Synthesis

Spinel Nanostructures for the Hydrogenation of CO2 to Methanol and Hydrocarbon Chemicals

Conversion of CO2 Hydrogenation to Methanol over K/Ni Promoted MoS2/MgO Catalyst

Mn-promoted MoS 2 catalysts for CO 2 hydrogenation: enhanced methanol selectivity due to MoS 2 /MnO x interfaces

Synthesis of Cobalt-Based Nanoparticles as Catalysts for Methanol Synthesis from CO2 Hydrogenation

Modifying Spinel Precursors for Highly Active and Stable Ni‐based CO2 Methanation Catalysts

Turning a Methanation Co Catalyst into an In–Co Methanol Producer

Enhanced methanol production via selective hydrogen utilization during CO2 hydrogenation over Co containing dual-atom doped oxide catalyst

Manganese Oxide as a Promoter for Copper Catalysts in CO2 and CO Hydrogenation

Effect of Cu and Zn on the performance of Cu-Mn-Zn/ZrO2 catalysts for CO2 hydrogenation to methanol

An Active Manganese Promoted Ni/Al2O3 Catalyst for Low Temperature CO2 Methanation

Highly Active and Stable Mixed-Phase In2O3-supported Ni Catalyst for CO2 Hydrogenation to Methanol

Enhanced Mn-Co synergies of manganese-cobalt spinel oxide for efficient aerobic oxidation of benzyl alcohol

COx hydrogenation to methanol and other hydrocarbons under mild conditions with Mo3S4@ZSM-5

Nickel-modified In2O3 with inherent oxygen vacancies for CO2 hydrogenation to methanol

A highly efficient Li-Cu/MoO x catalyst constructed by a precursor dispersion and alkali metal promotion stepwise regulation strategy for CO 2 hydrogenation to methanol reaction

Sulfur vacancy-rich MoS2 as a catalyst for the hydrogenation of CO2 to methanol

Carbon Dioxide Valorization into Methane Using Samarium Oxide-Supported Monometallic and Bimetallic Catalysts

CO2 Hydrogenation to Methanol over Mesoporous SiO2-Coated Cu-Based Catalysts

CO Hydrogenation over Nanometer Spinel-Type Co/Mn Complex Oxides Prepared by Sol-Gel Method