Abstract:Alkali Silica Reaction (ASR) is a common deterioration mechanism affecting many concrete structures of any type and age. Initially identified more than 60 years ago (Stanton, 1930), this mechanism is based on the chemical reactions between certain siliceous minerals present in the aggregate and the alkalinity of the concrete in the presence of moisture (internal RH). While certain deterioration patterns are clearly associated with ASR, such as gel exudation, aggregate expansion, and characteristic cracking, the material degradation can often be misdiagnosed to the untrained eye. In addition, certain elements of a structure can be severely affected while neighboring elements of the same batch/ mix design do not bear signs of deterioration or impact. Thus far, in situ field monitoring of ASR affected structures is related to moisture measurements, electrical resistivity, expansion, service life models are based on fracture mechanics of the aggregate. The impact to the concrete is loss of integrity, decreased compressive strength, shear and tensile strength. Some observed structures have split, with such force, that the concrete structure had cracks greater than 25mm where steel retention bands have split. The authors of this paper were engaged in two instances to provide service life assessments for ‘corrosion related degradation’ on ASR affected structures. In all instances the elements which were assessed were structural, load bearing elements, which if failed could pose a significant risk to owner, user, or end recipient. The need to develop an assessment technique for monitoring and service life assessments which are practical and efficient is being developed. The paper will discuss the development of the approach, from visual indicators identifying condition hierarchies, to long term condition monitoring for various concrete parameters combined with laboratory testing (expansion and residual alkalis) and mathematical modeling. Three case studies will be presented to illustrate conditions and process.

Microscopic assessment of ASR-affected columns after 20 years in service

Condition Assessment of Asr-Affected Reinforced Concrete Columns after Nearly 20 Years in Service

ASR: Practical investigative techniques and field monitoring systems used to assess ASR for service life modeling.

Acoustic Emission Study on the Damage Evolution of a Corroded Reinforced Concrete Column under Axial Loads

A visual condition assessment of a reinforced concrete railway bridge subject to alkali silica reaction (ASR) deterioration in Johannesburg

Acoustic Emission Analysis of Corroded Reinforced Concrete Columns under Compressive Loading.

Microscopic investigation of building materials affected by alkali-silica reaction

Mechanical Degradation of Reinforced Concrete Columns Corroded Under Sustained Loads

Evaluation of alkali–silica reaction damage in concrete by using acoustic emission signal features and damage rating index: damage monitoring on concrete prisms

Cracking Mechanism of Corroded Reinforced Concrete Column Based on Acoustic Emission Technique

Monitoring accelerated alkali-silica reaction in concrete prisms with petrography and electrical conductivity measurements

Reliability of the Damage Rating Index to Assess Condition of Concrete Affected by External Sulfate Attack

Assessment of Concrete Structures Affected by Alkali–Silica Reaction and Freeze–Thaw by Use of Ultrasonic Surface Wave Method

Integrative experimental and numerical study of ASR affected nuclear concrete containments

Diagnosis of durability-related problems in concrete structures through comprehensive analysis and non-destructive testing: a case study

Damage Generated and Propagated by the AAR Reactive Aggregate from Kingston, Ontario, Canada

Acoustic Emission Assessment of Corroded RC Columns Jointly Reinforced with Concrete Canvas and CFRP

Challenges related to structural modelling and assessment of concrete structures affected by alkali-silica reactions

Effect of Moisture History on ASR Expansion and Microstructural Properties

Experimental investigation of ASR-affected concrete – The influence of uniaxial loading on the evolution of mechanical properties, expansion and damage indices

Long-term ultrasonic monitoring of concrete affected by alkali-silica reaction