Abstract:Acoustic emission (AE) monitoring was employed to detect and identify the extent of degradation resulting from reinforcing steel corrosion in concrete structures. Reinforced concrete samples were subjected to an accelerated corrosion test and corroded until they reached five different levels of mass loss of steel: 1, 2, 3, 4, and 5 %. The corrosion activity of all samples was continuously monitored using attached piezoelectric AE sensors and a multichannel data acquisition system. The results obtained from AE monitoring were analysed and compared to those obtained from half-cell potential (HCP) measurements, the amount of anodic current passing with time, and concrete cover cracking. The study analysed AE signal strength parameters including cumulative signal strength, historic index [H(t)], and severity (Sr) to detect the corrosion initiation, and subsequently, to classify the extent of damage following the corrosion progression. The study also aimed to correlate these parameters to both the degree of mass loss and concrete cover crack width. The results showed that the AE signal strength parameters can be exploited to characterize different degrees of damage from corrosion initiation and up to 5 % steel mass loss. These parameters can be analysed to detect the corrosion initiation earlier than the HCP test. This study also presented damage classification charts that can be used to correlate the level of steel mass loss and/or crack width to the AE signal strength parameters. Given these points, the outcomes of this investigation are substantial for advancing the application of acoustic emission for structural health monitoring in concrete structures.

Acoustic Emission Study on the Damage Evolution of a Corroded Reinforced Concrete Column under Axial Loads

Acoustic Emission Analysis of Corroded Reinforced Concrete Columns under Compressive Loading.

Cracking Mechanism of Corroded Reinforced Concrete Column Based on Acoustic Emission Technique

Uniaxial Concrete Tension Damage Evolution Using Acoustic Emission Monitoring

Mechanical Degradation of Reinforced Concrete Columns Corroded Under Sustained Loads

Analytical Model for Concrete Jacketed RC Columns with Precorrosion and Postcorrosion Damages under Uniaxial Loading

Acoustic Emission Assessment of Corroded RC Columns Jointly Reinforced with Concrete Canvas and CFRP

Effects of Reinforcement Corrosion and Sustained Load on Mechanical Behavior of Reinforced Concrete Columns.

Acoustic Emission Analysis of Crack Type Identification of Corroded Concrete Columns under Eccentric Loading: A Comparative Analysis of RA-AF Method and Gaussian Mixture Model

Axial Loading Capacity Of Concrete-Jacketed Rc Columns With Pre- And Post-Corrosion Damage

Experimental Investigation on Seismic Behavior of Corroded RC Columns under Artificial Climate Environment and Electrochemical Chloride Extraction: A Comparative Study

Experimental investigation on the seismic performance of corroded reinforced concrete columns designed with low and high axial load ratios

Performance of Corroded Reinforced Concrete Columns under the Action of Eccentric Loads

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Time-Dependent Load Bearing Capacity of Corroded Rc Columns in Atmosphere Environment

Damage evaluation and failure mechanism analysis of steel tube confined reinforced-concrete columns by acoustic emission technology

Acoustic emission monitoring and damage assessment of FRP-strengthened reinforced concrete columns under cyclic loading

Evaluation of damage progression in concrete structures due to reinforcing steel corrosion using acoustic emission monitoring

Study on Degradation Regularity of Bearing Capacity of RC Beams under Corrosive Conditions

Damage analysis of concrete-filled square stainless steel columns based on acoustic emission and Markov chain methods

Fractal Signal Processing Method of Acoustic Emission Monitoring for Seismic Damage of Concrete Columns