Abstract:Steam is essential in petrochemical industries for the transportation of thermal energy and usage in some reforming process. Superheaters are heat exchangers that convert saturated steam to dry steam by utilizing waste heat from the flue gas stream. Medium pressure steam superheaters are prone to tube deterioration due to service at elevated temperatures and erosion from the presence of liquid phase in the steam, leading to tube plugging after tube failure. This reduces the overall surface heating area of the superheater. Relations between the tube plugging practice and the energy dynamics of the superheaters are important for engineers to identify the responses of the superheater for operation planning, and this issue has not been extensively explored academically. This article analyses the deterioration of superheater performance due to reduction of surface heating area based on operational data of a petrochemical steam generation line. The objective is to find relations between the effect of tube plugging on the states of both steam and flue gas streams, as well as its impact on the overall energy exchange. The operating conditions of a superheater at two separate service years, before (year 2014) and after (year 2017) tube plugging, were compared through the first law energy analysis. The average steam inlet temperatures were between 248 °C and 250 °C, at flow rates between 70 and 90 ton/hour. The analysis indicated that 0.3 to 0.8 % increase in inlet energy is required for every plugged tube to compensate for the reduction of heating surface. At 3 % reduction of heating surface area, the heat exchanger effectiveness decreases by an average of 11 % that also leads to a lower steam temperature output by approximately 6% from the design operating temperature. These results would assist steam engineers to analyse changes to the energy economics of the whole plant and decide the feasibility of replacing existing superheaters with new ones. Also, another significant finding to be considered by steam engineers is that the current practice of increasing the steam flow rate does not offset the loss of energy effectiveness due to tube plugging.

Case Study on Fireside Erosion of Platen Superheater Boiler Tubes of a Coal-Fired Power Plant

Failure Analysis of T91 Finish Superheater Tube in 660 MW Supercritical Thermal Power Plant

Failure Analysis of Utility Boiler Superheater Tubes of A213 T12

Failure analysis of reheater tubes in a 350 MW supercritical circulating fluidized bed boiler

Coal-Ash Corrosion of a Chromium-Molybdenum Steel Superheater Tube

Failure Analysis of Stainless Steel Heat Exchanger Tubes in a Petrochemical Plant

Metallurgical Failure Analysis of Economizer Tube of Thermal Power Plant

Cause Analysis of Superheater Tube Cracking in Medium Temperature Separated Circulating Fluidized Bed Boiler

Microstructural Evolution and Oxidation Resistance of T92 Boiler Tube Steel Upon Long-Term Supercritical Steam Test

Corrosive damage analysis and characterization of boiler tubes in a secondary superheater

Water Wall Tubes’ High Temperature Corrosion Root Cause Investigation: A 300 MW Level Boiler Case

Failure analysis of oil refinery heater treater's fractured fire tube

Failure analysis of steam superheater boiler tube made of ASTM T22 steel

Corrosion and Fouling of Heat Transfer Surfaces

High-temperature corrosion data and mechanisms for T122, Super304H and HR3C after 15 years in 1000MW ultra-supercritical power plant

Performance degradation analysis of a medium pressure superheater due to tube deactivation

Failure Analysis on Abnormal Corrosion of Economizer Tubes in a Waste Heat Boiler

High-Temperature Degradation and Protection of Ferritic and Austenitic Steels in Steam Generators

Analysis of the Causes of the Emergency Shutdown of Natural Gas-Fired Water Peak Boilers at the Large Municipal Combined Heat and Power Plant