Abstract:The resistivity of the sintered Cu thick film decreases with the weight percentage of the SiO2‐ZnO‐B2O3 additive in the mixing glass frits up to 50 wt.%. As the weight percentage of the SiO2‐ZnO‐B2O3 additive in the mixing glass frits is over 50 wt.%, the resistivity of the sintered Cu thick films is quite similar. The lowest resistivity (6.62x10‐6 Ω‐cm) of the sintered Cu thick films occurs at 75 wt.% of the SiO2‐ZnO‐B2O3 additive. Also, we observe the extensive glass phase framing around the large Cu grains in the Cu thick films sintered with low SiO2‐ZnO‐B2O3 additives (less than 50 wt.%) narrows the cross‐section area of the electrical path. On the contrary, the round‐shaped glass phase solidified among the small Cu grains allows a larger cross‐section of the electrical path (a possible lower resistivity) for the Cu thick films sintered with higher SiO2‐ZnO‐B2O3 additives (larger than 50 wt.%). The above results imply that the resistivity of the sintered Cu thick film correlates well with the microstructure (Cu grain size and the glass/Cu composite structure) of the sintered Cu thick films.Twin grain boundaries can clearly be observed in the sintered Cu thick films, especially for the Cu thick film sintered with the higher SiO2‐ZnO‐B2O3 additives. Owing to small Cu grains size and high density of Cu grain boundary, the probability of the grain boundaries with a high grain‐boundary energy in the Cu thick film sintered with high SiO2‐ZnO‐B2O3 additive would be much larger, comparing to that in the Cu thick film sintered with low SiO2‐ZnO‐B2O3 additive. Thus, more annealing twin boundaries formed in the Cu thick film sintered with high SiO2‐ZnO‐B2O3 additive. Hence, the formation of the twin boundary in the sintered Cu thick film helps reducing the resistivity of the sintered Cu films.

Submicron Cu@glass core-shell powders for the preparation of conductive thick films on ceramic substrates

Preparation and properties of antioxidative BaO–B2O3–SiO2 glass-coated Cu powder for copper conductive film on LTCC substrate

Facile synthesis and electrical performance of silica-coated copper powder for copper electronic pastes on low temperature co-fired ceramic

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Effect of properties and crystallization behavior of BaO‐ZnO‐B 2 O 3 ‐SiO 2 glass on the electrical conductivity of Cu paste

Facile fabrication and low-temperature bonding of Cu@Sn–Bi core–shell particles for conductive pastes

Thermal Sintering Matchability Between Low‐Temperature Cofired Ceramic Substrate and Silver Pastes and the Effect of CuO on Silver Diffusion Inhibition

Powder metallurgy process enables production of high-strength conductive Cu-based composites reinforced by Cu50Zr43Al7 metallic glass

Thermal Sintering Matchability between LTCC Substrate and Silver Pastes and the Effect of CuO on Silver Diffusion Inhibition

Study on Low-Temperature Conductive Silver Pastes Containing Bi-Based Glass for MgTiO3 Electronic Power Devices

Structure and Properties of Electrocodeposited Cu-Al2o3 Nanocomposite Thin Films

Formation of a Highly Conductive Thick Film by Low-Temperature Sintering of Silver Paste Containing a Bi2O3-B2O3-ZnO Glass Frit

Preparation of B2O3-ZnO-SiO2 Glass and Sintering Densification of Copper Terminal Electrode Applied in Multilayer Ceramic Capacitors

Optimizing mechanical and electrical properties of Cu-coated Cu–Zr–Al bulk metallic glass composites by adjusting glassy powder size

Al₂O₃-Cu Substrate with Co-Continuous Phases Made by Powder Sintering Process

Effects of viscosity and wettability of Pb-B-Si-O glass in silver paste on the co-firing densification of LTCC

Investigation of Ethylene Glycol, Α-Terpineol, and Polyethylene Glycol 400 on the Sintering Properties of Cu–Ag Core–shell Micro/nano-Mixed Paste

Particle size modulation for effectively optimizing the dielectric and mechanical properties of La2O3–B2O3 based glass-ceramic/ceramic LTCC substrates

Effect of mixing glass frits on electrical property and microstructure of sintered Cu conductive thick film

Preparation of Conducting Films with High Performance

Cu Particulate Dispersed Cu50Zr45Al5 Bulk Metallic Glassy Composite with Enhanced Electrical Conductivity