Abstract:In this study, friction stir welding (FSW) was employed to join AA3003-H18 sheets by incorporating in situ Al-Cu intermetallic compounds within the stir zone. The FSW process was carried out under three distinct conditions: (I) without applying powder, (II) by introducing Cu powder, and (III) by incorporating Cu-Al mixed powder (50 vol.% Cu, 50 vol.% Al). The powder was embedded into the gap between two sheets. Subsequently, two-pass FSW, involving both forward and backward movements, was conducted with a rotational speed of 1200 rpm and traverse speed of 100 mm/min across all three experimental conditions. In the second and third conditions, the formation of in situ intermetallic compounds occurred through a solid-state reaction between Cu particles and Al within the stir zone. Examination of the stir zone through optical and electron microscopic studies revealed that the utilization of Cu-Al mixed powder resulted in finer and more uniformly distributed Cu clusters and Al-Cu intermetallics than samples welded with Cu powder alone. Notably, the stir zone of samples incorporating Cu-Al mixed powder exhibited finely dispersed, completely gray Al-Cu intermetallic particles, whereas those with only Cu powder displayed predominantly coarse core-shell particles in the microstructure. The introduction of Cu-Al mixed powder during FSW resulted in a stir zone with an average hardness of 74 HB, showing a 14% increase compared to the cases where Cu powder alone was added (65 HB). Tensile tests, conducted in both transverse and longitudinal directions on the FSWed samples, did not exhibit a consistent trend across the three mentioned conditions. Transverse tensile strength consistently ranged between 107 and 110 MPa, with joint efficiency varying from 52% to 54%. However, the longitudinal tensile strength of the joint with added Cu-Al mixed powder (158 MPa) surpassed those welded with Cu powder alone (134 MPa).

Preparation of bimetallic nano-composite by dissimilar friction stir welding of copper to aluminum alloy

Nanoparticles Addition in AA2024 Aluminum/Pure Copper Plate: FSSW Approach, Microstructure Evolution, Texture Study, and Mechanical Properties

In-situ nanocomposite in friction stir welding of 6061-T6 aluminum alloy to AZ31 magnesium alloy

Effect of Nano Particle Deposition on Mechanical Properties of Friction Stir Welded Dissimilar Aluminium Alloys by Taguchi Technique

Effect of Dispersing In Situ Al-Cu Intermetallic Compounds on Joint Strength in Friction Stir Welding of AA3003-H18 Sheets

Dissimilar friction stir welding of 7075 aluminum alloy to AZ31 magnesium alloy using SiC nanoparticles

Microstructural characterization and mechanical properties of micro friction stir welded dissimilar Al/Cu ultra-thin sheets

Investigation of Mechanical Properties on Underwater Friction Stir Welded AA7075 With Pure Copper Dissimilar Joints

Microstructure and Mechanical Properties Analysis of Al/Cu Dissimilar Alloys Joining by Using Conventional and Bobbin Tool Friction Stir Welding

Material Flow Behavior and Thermal Cycle during Friction Stir Welding of AA5083/AZ91 Dissimilar Metals

Effect of TiO2 nanoparticles addition on microstructure and mechanical properties of dissimilar friction stir welded AA6063-T4 aluminum alloy and AZ31B-O magnesium alloy

Metallurgical and Mechanical Properties of Al–Cu Joint by Friction Stir Spot Welding and Modified Friction Stir Clinching

Microstructural Characterisation and Mechanical Properties of Dissimilar AA5083-copper Joints Produced by Friction Stir Welding

Combined effect of nanocompositing and addition of interlayer on friction stir welding of aluminum/magnesium joint: a study

Intermetallic Compounds Formation in Dissimilar Friction Stir Welding of Mg/Cu Alloys

Investigations into the formation of intermetallic compounds during pinless friction stir spot welding of AA2024-Zn-pure copper dissimilar joints

Experimental Review on Friction Stir Welding of Aluminium Alloys with Nanoparticles

Influence of FSW process on dissimilar T-joint of aluminum alloy to pure copper

Joining of Dissimilar Al and Mg Metal Alloys by Friction Stir Welding

Microstructure and XRD Analysis of FSW Joints for Copper T2/aluminium 5A06 Dissimilar Materials

Experimental Investigation and Characterization of Friction Stir Spot-Welded Dissimilar Aluminum Copper Metallic Lap Joints