Abstract:As tellurides and selenides of Bismuth are extensively used thermoelectric materials in the low-temperature range with refrigeration application, A concerted effort is put forth to boost the ZT by co-doping the pristine Bi 2 Se 3 with antimony (Sb) on cation end and tellurium (Te) on anion side of the compound. The double sintered solid-state reaction method is employed in the preparation of Bi 2 Se 3 and (Bi 1− x Sb x ) 2 Se 2.7 Te 0.3 polycrystalline pellets, with x = 0.02, 0.04, and 0.06. The sample exhibits a rhombohedral structure with the space group of R m. FESEM and EDAX analysis are used to confirm surface morphology and elemental composition of the produced samples. The thermoelectric measurements for the pristine and co-doped samples were conducted by the physical property measurement system as well as a considerable increase in the Seebeck coefficient of − 115 μV/K is observed for 0.02 doping of the Sb which is 4.2 times greater than as for pristine (S = − 28 μV/K). Higher concentration doping ( x = 0.04, 0.06) has not reflected any Seebeck coefficient advancement. In contrast, the lowest total thermal conductivity at a low-temperature regime (< 50 K) is observed for x = 0.06 doping concentration which at near room temperature increases beyond the pristine thermal conductivity; whereas, x = 0.02, 0.04 doping concentration shows a decrement in total thermal conductivity at low, at room temperature region the values are almost equivalent to that of pristine. The co-doped samples' electrical resistivity is substantially less than pristine sample. The highest power factor of 3 × 10 –4 μW/mK 2 is obtained for the x = 0.02 sample. The highest ZT value for the x = 0.02 sample is almost 28 times more than a pristine sample. We conducted a study where we combined experimental and DFT methods to investigate thermoelectric properties incorporated into pristine and doped with antimony and tellurium on Bi 2 Se 3 . We have employed this combination to investigate the partial density of states, Seebeck coefficient, power factor using the Boltzmann transport equation. Theoretical thermoelectric data were derived and compared to experimental observations. Hence, using combined experimental and theoretical investigations helps to predict with higher accuracy of thermoelectric properties of semiconducting materials.

Transport Property Measurements in Doped Bi2Te3 Single Crystals Obtained via Zone Melting Method

A comprehensive experimental and DFT analysis on thermoelectric properties of Sb, Te co-doped Bi2Se3 polycrystals

The transport properties of Nb-doped trichalcogenide Ta0.8Nb0.2S3

Electronic Transport Studies of Ag-doped Bi2Se3 Topological Insulator

Transport and electrical properties of cryogenic thermoelectric FeSb2: the effect of isoelectronic and hole doping

Thermoelectric Properties of I-doped Bi2Te2.85Se0.15 Solid Solutions

Crystal structure and thermoelectric properties of bulk polycrystalline (SbxBi1-x)2Se3 alloys

Preparation and Thermoelectric Properties of Doped Bi 2 Te 3 -Bi 2 Se 3 Solid Solutions

Anisotropic thermoelectric transport properties of Bi0.5Sb1.5Te2.96+x zone melted ingots

Simultaneous Regulation of Electrical and Thermal Transport Properties of N-Type Bi2Te3 Via Adding Excessive Te Followed by Se Doping

Transport Properties of SnTe–Bi2Te3 Alloys

Electronic Transport and Thermoelectric Properties of Te-Doped Tetrahedrites Cu12Sb4-yTeyS13

Investigation of thermoelectric and magnetotransport properties of single crystalline Bi2Se3 topological insulator

Doping Effect on Thermoelectric Properties of Nonstoichiometric AgSbTe 2 Compounds

Ambipolar surface state transport in non-metallic stoichiometric Bi$_2$Se$_3$ crystals

Carrier density dependence of the magnetic properties in iron-doped Bi2Se3 topological insulator

Enhanced Thermoelectric Properties in Highly Co-Doped Bi2Se3 by Density-of-State Effective Mass Increase

Improvement in thermoelectric properties of Bi-Mg co-doped SnTe via band engineering and nanostructuring

Uniformity of Thermoelectric Properties of N-type Bi<sub>2</sub>Te<sub>3-y</sub>Se<sub>y</sub> Bulky Compacts

Unusual non saturating Giant Magneto-resistance in single crystalline Bi2Te3 topological insulator

Low-carrier-concentration Crystals of the Topological Insulator Bi2Te2Se