Abstract:In the present research an Al–7.7%Mn–4.9%Zr–3.2%Cu (wt%) alloy was processed by mechanical alloying (MA) followed by hot press sintering. The microstructure, phase composition, and mechanical properties of the MA granules and sintered samples were investigated. The dissolution of Mn, Zr, and Cu with further precipitation of the Al6Mn phase were observed during high-energy ball milling. In the alloy processed without stearic acid after milling for ~10 h, an Al-based solid solution with ~4.9 wt%Zr, ~3.2 wt%Cu and a ~5 wt%Mn with a grain size of ~16 nm and a microhardness of ~530 HV were observed. The addition of stearic acid facilitated Mn dissolution and precipitation of the Al6Mn phase during milling but led to the formation of the ZrH2 phase that decreased the Zr solute and the microhardness. Precipitation of the Al6Mn, L12–Al3Zr, and Al2Cu phases during annealing and sintering of the MA granules in the temperate range of 350–375 °C was observed, and an additional Al20Cu2Mn3 phase was precipitated at 400–450 °C. Hot-press sintering at 450 °C provided a low fraction of cavities of ~1.5%, the yield strength of 1100 MPa, ultimate compressive strength of 1200 MPa, strain at fracture of 0.5% at room temperature, the yield strength of 380 MPa, ultimate compressive strength of 440 MPa, and strain at fracture of 3.5% at 350 °C. The microstructural evolution during high-temperature deformation on the sample surface was studied and the differences in deformation behavior for the alloys sintered at different temperatures were discussed.

Alloying of Al2Au intermetallic compound with Cu by the ball milling technique

The Effect of A Small Amount of Tungsten on the Microstructure of Mechanically Alloyed Ag37cu63

Cu-63 Nmr-Study Of Cu83-Zn17 Mixed Powders During Mechanical Alloying

Amorphization in the AlC System by Mechanical Alloying

63Cu NMR Study of Cu83-Zn17Mixed Powders During Mechanical Alloying

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

Nanostructured Composite Obtained by Mechanically Driven Reduction Reaction of Cuo and Al Powder Mixture

Reduction reaction in Al-CuO powder mixture driven by mechanical alloying

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

The Influence of Ball Milling Conditions on the Powder Characteristics and Sintering Densification of Mo-Cu Alloy

Influence of Ball-Milling with Cu Powder on Electrochemical Properties of V-based Solid Solution Type Hydrogen Storage Alloys

Study on Microstructure and Properties of Cu-Zr Alloy Prepared by Mechanical Alloying

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

EFFECTS OF HIGH-ENERGY BALL MILLING ON THE STRUCTURE AND PROPERTY OF A MULTIPHASE Al3Ti-BASED INTERMETALLIC ALLOY

Metastable Structures of Immiscible System Induced by Mechanical Alloying

Preparation of FeAl (B2) intermetallic powder by ball milling and heat treatment

63Cu Nuclear Magnetic Resonance Analysis of Mechanical Alloying Processes in Copper-Zinc Powders

Effect of high energy ball milling on the displacement reaction in particulate reinforced Al–Si–Cu alloy matrix composite powders

Properties of High-Entropy Fe30Co20Ni20Mn20Al10 Alloy Produced by High-Energy Ball Milling

Superstructure in nano-crystalline Al50Cu28Fe22 alloy

The Microstructure and Properties of Al–Mn–Cu–Zr Alloy after High-Energy Ball Milling and Hot-Press Sintering