Abstract:The effect of coating cracking during depth-sensing indentation testing (e.g. nanoindentation testing) on systems comprising thin hard coatings (e.g. TiN) on a less stiff, hard substrate (e.g. steel) has been investigated in order to establish whether, at such small scales, the occurrence of annular through-thickness cracks around indentation sites can be detected from load–displacement plots and whether any accompanying localized debonding of the coating from the substrate can also be identified. Experiments were performed on thin TiN and NbN monolayers, and compositionally modulated TiN/NbN and TiN/ZrN deposited onto hard steel or stainless steel substrates. Above a critical load (Pcrit) in the range 80–500mN, all systems exhibited annular through-thickness cracks around indentation sites. The cracking was found to be accompanied by a discrete change in gradient of the loading portion of the load–displacement curve. Also, analysis of the unloading curves beyond this point showed that elastic recovery was controlled by the elastic modulus of the underlying substrate material alone. The cracking mechanism has been characterized using scanning electron microscopy, coupled with optical profilometry to map the detailed z-displacement of the surface — a procedure critical to understanding whether coating–substrate debonding had occurred. Some cracks were found to show a spiral morphology and the effect of indentation loading rate was investigated to see if appearance of these cracks was loading-rate sensitive. Our results highlight the problems inherent in assessing both the interfacial failure and the interfacial fracture toughness of thin film coated systems at the small contact scales (⩽1μm) associated with crack genesis where it is difficult to confirm the extent of sub-surface cracks by conventional means. We have also demonstrated that both load–displacement and load–displacement squared plots are necessary if a more complete understanding of system behaviour is to be gained. Also, a simple fracture mechanics model for the annular cracking behaviour seen in such systems has been derived and used to estimate a value of Gic (the interfacial work of fracture) as 180Jm−2 for the TiN/ZrN-stainless steel system.

Cross-sectional nanoindentation (CSN) studies on the effect of thickness on adhesion strength of thin films

Adhesion strength of ductile thin film determined by cross-sectional nanoindentation

Numerical studies on deformation and adhesion behaviour of substrate during nanoindentation

Residual Stresses And Debonding Of Diamond Films On Titanium Alloy Substrates

Film Thickness Effects on Mechanical and Tribological Properties of Nitrogenated Diamond-Like Carbon Films

The effect of coating cracking on the indentation response of thin hard-coated systems

Superlayer Residual Stress Effect on the Indentation Adhesion Measurements

Determination of Adhesion Energy of CNx Thin Film on Silicon from Micro-Scratch Testing

Indentation stress–strain analysis and finite element simulation to determine elastoplastic properties of thin films decreasing the substrate contribution

Quantitative investigation of the adhesion failure of Ti-based metal thin films on Si wafers

Substrate effect and nanoindentation fracture toughness based on pile up and failure

Adhesion and debonding of multi-layer thin film structures

Intensified chipping during nanoindentation and the effect of friction on the interfacial fracture for thin films used in N/MEMS

Microstructure, mechanical and tribological properties Of A-C/A-C:Ti nanomultilayer film

Indentation of Coatings at micro/nano scale: Crack formation and deflection

The study of anisotropic behavior of nano-adhesive contact by multiscale simulation

Influence of Nitrogen Implantation on Adhesion Strength of TiAlN Film on Γ-Tial Alloy

Cracks at shallow nanoindentation depths in titanium diboride hard thin coatings used in AFM nanoindentation☆

Effect of microstructure on the adhesion strength of TiB coating on Ti6Al4V substrate

The effect of the substrate on the mechanical properties of TiN coatings

Effect of the TiSiN interlayer properties on the adhesion and mechanical properties of multilayered TiSiCN thin films