Abstract:The effect of coating cracking during depth-sensing indentation testing (e.g. nanoindentation testing) on systems comprising thin hard coatings (e.g. TiN) on a less stiff, hard substrate (e.g. steel) has been investigated in order to establish whether, at such small scales, the occurrence of annular through-thickness cracks around indentation sites can be detected from load–displacement plots and whether any accompanying localized debonding of the coating from the substrate can also be identified. Experiments were performed on thin TiN and NbN monolayers, and compositionally modulated TiN/NbN and TiN/ZrN deposited onto hard steel or stainless steel substrates. Above a critical load (Pcrit) in the range 80–500mN, all systems exhibited annular through-thickness cracks around indentation sites. The cracking was found to be accompanied by a discrete change in gradient of the loading portion of the load–displacement curve. Also, analysis of the unloading curves beyond this point showed that elastic recovery was controlled by the elastic modulus of the underlying substrate material alone. The cracking mechanism has been characterized using scanning electron microscopy, coupled with optical profilometry to map the detailed z-displacement of the surface — a procedure critical to understanding whether coating–substrate debonding had occurred. Some cracks were found to show a spiral morphology and the effect of indentation loading rate was investigated to see if appearance of these cracks was loading-rate sensitive. Our results highlight the problems inherent in assessing both the interfacial failure and the interfacial fracture toughness of thin film coated systems at the small contact scales (⩽1μm) associated with crack genesis where it is difficult to confirm the extent of sub-surface cracks by conventional means. We have also demonstrated that both load–displacement and load–displacement squared plots are necessary if a more complete understanding of system behaviour is to be gained. Also, a simple fracture mechanics model for the annular cracking behaviour seen in such systems has been derived and used to estimate a value of Gic (the interfacial work of fracture) as 180Jm−2 for the TiN/ZrN-stainless steel system.

Substrate effect and nanoindentation fracture toughness based on pile up and failure

Measuring elastoplastic properties of thin films on an elastic substrate using sharp indentation

Exploration of the Origin of Substrate Effects and Elastic Strain Properties During Thin Film Nanoindentation

Nanoindentation stress-strain for Fracture Analysis and computational modeling for hardness and modulus

Indentation of Coatings at micro/nano scale: Crack formation and deflection

A novel approach to extracting hardness of copper/niobium (Cu/Nb) multilayer films by removing the substrate effect

In Situ Nanoindentation Mechanical Property of Films by Atomic Force Microscope

Quantitative In-Situ Study of Strength-Governed Interfacial Failure Between H-Bn and Polymer-Derived Ceramic

Effects of the Substrate on the Determination of SEBS Thin Film Mechanical Properties by Nanoindentation

Intensified chipping during nanoindentation and the effect of friction on the interfacial fracture for thin films used in N/MEMS

Influence of substrate type on deformation specificity of soft film/hard substrate coated systems under nanomicroindentation

The effect of coating cracking on the indentation response of thin hard-coated systems

Cracks at shallow nanoindentation depths in titanium diboride hard thin coatings used in AFM nanoindentation☆

Indentation stress–strain analysis and finite element simulation to determine elastoplastic properties of thin films decreasing the substrate contribution

A Nanoindentation Study of the Deformation Mode for Nanostructured Ductile/brittle Multilayers: Cracking Versus Shear Banding

Correction of Substrate-Induced Thin-Film Modulus Deviations in Nanoindentation Measurements

Identifying the elastoplastic properties of ductile film on hard substrate by nanoindentation

Analysis of deformation behaviour of Al–Ni–Co thin film coated aluminium during nano-indentation: a molecular dynamics study

Physical phenomena during nanoindentation deformation of amorphous glassy polymers

Surface Effects on the Spherical Indentation of Biological Film/substrate Structures

Nano-Indentation for Characterizing Mechanical Properties of Soft Materials