Abstract:The effects of subtransus treatment (750 degrees C, 800 degrees C, 850 degrees C, 900 degrees C, and 950 degrees C) as well as supertransus treatment (1100 degrees C) on the microstructures and mechanical performance of electron beam welded (EBW) joints of laser powder bed fusion (LPBF) TC11 alloy were investigated. At a solution temperature of 950 degrees C, globular alpha phases and transformed beta phases were observed in the joint. When the solution temperature exceeded the beta transus temperature (T beta), alpha colonies and massive alpha phases emerged in the joints, resulting in Widmanstatten structures. The base metal (BM) exhibited the highest microhardness, followed by the heat affected zone (HAZ), whereas the fusion zone (FZ) demonstrated the lowest microhardness. As the solution temperature increases, the microhardness of joints decreases at first and then increases. Notably, the joint subjected to a solution temperature of 850 degrees C exhibited the lowest microhardness. When the solution temperature was >= 900 degrees C, transformed beta phases emerged within the joints, resulting in an elevation of microhardness. Below T beta , the elongation of welded joints gradually augmented while the tensile strength reduced at first and then increased with the rising solution temperature. Microstructures in joint with solution temperature of 950 degrees C consisted of lamellar alpha phases, globular alpha phases, and transformed beta phases. As a result, the joint exhibited an optimal balance between strength (1103.1 +/- 34.9 MPa) and plasticity (9.37 +/- 0.20%). Ductile fracture characteristics with dimples on the fracture surface were observed in the tensile samples. Therefore, it can be concluded that a solid solution temperature of 950 degrees C is optimal for LPBF TC11 alloy.

Microstructure-Mechanical Properties Relation of TLP-Bonded FSX-414 Superalloy: Effect of Homogenization Design

Effect of transient liquid phase bonding followed by homogenization on the microstructure and hot tensile behavior of Inconel 738 superalloy

Influence of transient liquid phase bonding followed by homogenization on the fatigue lifetimes of inconel 738 at elevated temperature

TLP repaired IN738LC superalloy with uneven surface defect gap width after post heat treatment: Microstructure and mechanical properties

Effect of holding time on microstructure and mechanical properties of dissimilar γ'‐strengthened superalloys TLP joint

Transient Liquid Phase Bonding of ZGH451 Superalloy Fabricated by Directed Energy Deposition

Homogenization Treatment-Induced Reduction of Brittle Intermetallic Compounds in Ti2alnb/Ti60 Brazed Joints: Effect on Microstructure and Mechanical Properties

Improving Tensile Properties of Dissimilar TLP Bonding Joints of IN718 Nickel-Based Superalloy/316LN Austenitic Steel by Long-Term Post-bonded Homogenization Treatment

Effect of Bonding Time on Dissimilar Transient Liquid Phase (TLP) Bonding of IN939 to IN625 Superalloys: Microstructural Characterization and Mechanical Properties

A Study on the Effect of Process Parameters on the Properties of Joint in TLP-Bonded Inconel 738LC Superalloy

Experimental and Numerical Study of Transient Liquid Phase Diffusion Bonded DZ40M Superalloys

Evolution of microstructure and mechanical properties on dissimilar transient liquid phase (TLP) bonding of GTD-111 and IN-718 by BNi-9 (AWS A5.8/A5.8M) interlayer

Microstructure and brazing mechanism of TiAl/Ni-based superalloy joints using Ti-Zr-Cu-Ni-Co-Mo-B filler metal with different cooling rates

Different Heat-Exposure Temperatures on the Microstructure and Properties of Dissimilar GH4169/IC10 Superalloy Vacuum Electron Beam Welded Joint

Transient Liquid Phase Diffusion Bonding of Ni3Al Superalloy with Low-Boron Nickel-Base Powder Interlayer

Microstructural Evolution and Mechanical Properties of Ti2AlNb/GH99 Superalloy Brazed Joints Using TiZrCuNi Amorphous Filler Alloy

Homogenization timing effect on microstructure and precipitation strengthening of 17–4PH stainless steel fabricated by laser powder bed fusion

Homogenization heat treatment of 2099 Al–Li alloy

Influences of Solution Temperature on Microstructures and Performance of Electron Beam Welded Joints of Laser Powder Bed Fusion TC11 Thin-Walled Samples

Microstructural Evolution and Kinetics of 7075 Al Alloy During Homogenization Treatment

Influence of Various Heat Treatments on Microstructures and Mechanical Properties of GH4099 Superalloy Produced by Laser Powder Bed Fusion