Different Heat-Exposure Temperatures on the Microstructure and Properties of Dissimilar GH4169/IC10 Superalloy Vacuum Electron Beam Welded Joint

Hualin Cai,Zhixuan Ma,Jiayi Zhang,Liang Qi,Jinbing Hu,Jiayi Zhou
DOI: https://doi.org/10.3390/met14030348
IF: 2.695
2024-03-18
Metals
Abstract:Vacuum electron-beam welding (EBW) was used to join the precipitation-strengthened GH4169 superalloy and a new nickel-based superalloy IC10 to fabricate the turbine blade discs. In this study, a solid solution (1050 °C/2 h for GH4169 and 1150 °C/2 h for IC10) and different heat-exposure temperatures (650 °C, 750 °C, 950 °C and 1050 °C/200 h, respectively) were used to study the high-temperature tensile properties and microstructure evolution of welded joints; meanwhile, the formation and evolution of the second phases of the joints were analyzed. After EBW, the welded joint exhibited a typical nail morphology, and the fusion zone (FZ) consisted of columnar and cellular structures. During the solidification process of the molten pool, Mo elements are enriched in the dendrites and inter-dendrites, and that of Nb and Ti elements was enriched in the dendrites, which lead to forming a non-uniform distribution of Laves eutectic and MC carbides in the FZ. The microhardness of the FZ gradually increased during thermal exposure at 650 °C and reached 300–320 HV, and the γ′ and γ′′ phases were gradually precipitated with size of about 50 nm. Meanwhile, the microhardness of the FZ decreased to 260–280 HV at 750 °C, and the higher temperature resulted in the coarsening of the γ′′ phase (with a final size of about 100 nm) and the formation of the acicular δ-phase. At 950 °C and 1050 °C, the microhardness of FZ decreased sharply, reaching up to 170~190 HV and 160~180 HV, respectively. Moreover, the Laves eutectic and MC carbides are dissolved to a greater extent without the formation of γ′′ and δ phases; as a result, the absent of γ′′ and δ phases are attributed to the significant improvement of segregation at higher temperatures.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
This paper mainly discusses the influence of different heat exposure temperatures on the microstructure and properties of GH4169/IC10 dissimilar nickel-based superalloy electron beam welded joints. In the study, the authors used solution treatment (1050°C/2 hours for GH4169, 1150°C/2 hours for IC10) and different heat exposure temperatures (650°C, 750°C, 950°C, and 1050°C/200 hours) to investigate the high-temperature tensile properties and microstructural evolution of the welded joints. After welding, the joint presented a nail-shaped morphology, and the fusion zone (FZ) consisted of columnar and cellular structures. During the solidification process of the weld pool, Mo element enriched in dendrites and interdendritic regions, while Nb and Ti elements enriched in dendrites, resulting in uneven distribution of Laves eutectic and MC carbides. As the heat exposure temperature increased from 650°C to 1050°C, the microhardness of the FZ first increased and then significantly decreased, accompanied by the precipitation, refining, or coarsening of γ' and γ'' phases. The paper pointed out that high-temperature heat exposure could lead to the transformation of γ'' phase, such as the formation of needle-like δ phase at 750°C, while the dissolution of Laves eutectic and MC carbides and the absence of γ'' and δ phases at 950°C and 1050°C were attributed to higher temperature-induced larger diffusion. These changes affected the mechanical properties of the joint, such as tensile strength and hardness. The study also indicated that electron beam welding (EBW) could effectively reduce the formation of harmful phases and had a narrow heat-affected zone, making it an ideal method for connecting IC10 and GH4169 alloys. By analyzing the structural evolution of welded joints under different heat exposure conditions, the paper aims to provide a theoretical basis for the study of the service performance of integral blisks.