Abstract:A large range of iron-carbon alloys were investigated under milling conditions. The alloy systems used included AISI 1020 mild steel, high-carbon low-alloy forged steel, forged martensitic stainless steel, forged austenitic stainless steel and NiHard, 20% chromium, 27% chromium, 30% chromium white cast irons. A range of mineral slurries was also used which included a corrosive copper-nickel sulfide ore, abrasive quartzite, taconite, molybdenite, and abrasive and corrosive quartzite-pyrrhotite combinations. These ranges of alloy systems and minerals provided suitable comparisons with respect to corrosive and/or abrasive conditions of the mineral slurry together with a suitable variation in microstructural constituents of the ball.Marked-ball wear tests were conducted under laboratory conditions in the main, but a small investigation aimed at identifying the importance of impact was also conducted using large industrial tumbling mills. Seven wear mechanisms were identified from examination of ball surfaces, using scanning electron microscopy. It was determined that wear rate was dependent upon a complex interaction of parameters involving microstructure, hardness ratio of the ball to the mineral, mineral slurry chemistry and pH and oxygen potential, ball mix and size. Adiabatic shear bands were also found in balls which were used in the large industrial mill. A galvanic series of the minerals and grinding media materials was determined from electrochemical tests, indicating the tendency of each grinding material to corrosive wear. The effect of media composition and microstructure was also determined using a strain index method developed in this investigation. In all the tests conducted the harder grinding media produced the most efficient grinding.Wet grinding efficiency was found to be dependent on media hardness, while wear under wet grinding was much higher, in general, than that under dry grinding. With respect to mill size it was found that the smaller laboratory mills tended to overemphasise corrosive wear compared with the larger laboratory mills.

Influence of Particle Size of Wheat Powder on Roller Wear Properties

Experimental Research on the Effect of Grinding Parameters on Ceramic Machined Surface Roughness

Exploring the Effect of Nanoparticle Size on the Tribological Properties of Sio2 / Polyalkylene Glycol Nanofluid under Different Lubrication Conditions

Grain size effect on abrasive wear mechanisms in alumina ceramics

Laboratory Investigation on the Particle-Size Effects in Railway Sanding: Comparisons Between Standard Sand and Its Micro Fragments

Effect of abrasive particle size and the influence of microstructure on the wear mechanisms in wear-resistant materials

Size Effect of Impact Abrasive Particles on Wear and Surface Hardening Behavior of High-Manganese Steel

Effect of Grain Size on the Tribological Behavior of CoCrFeMnNi High Entropy Alloy

Analysis and Evaluation of the Synergistic Effect of Ceramic Materials and Surface Texture on Anti-Abrasive Particle Wear under Rolling Conditions

Factors affecting wear in tumbling mills: Influence of composition and microstructure

Wear and damage transitions of two kinds of wheel materials in the rolling-sliding contact

Particle type effect on mechanisms of surface texturing in reducing wear

Friction and Wear Characteristics of the Polyer Powder Coatings for Solid Lubrication under the Dry Rolling/Sliding Condition

Effect of Grain Size on the Adhesive and Ploughing Friction Behaviours of Polycrystalline Metals in Forming Process

Analytical modeling of particle size effect on impact wear deformation characteristics of ductile materials

Modeling Analysis of Abrasive Wear

Effects of Abrasive Material and Hardness of Grinding Wheel on Rail Grinding Behaviors

Wear Mechanism of Ceramic Microbeads As Grinding Media

Three-Body Abrasive Wear Behavior of WC-10Cr3C2-12Ni Coating for Ball Mill Liner Application

The Role of Oxide-Scale Microtexture on Tribological Behaviour in the Nanoparticle Lubrication of Hot Rolling

Tribological mechanisms of slurry abrasive wear